Method for producing liquid crystal display apparatus

ABSTRACT

To provide a liquid crystal display apparatus exhibiting optimum display performance despite reduction in the number of PR(photolithography) processes, and a method for producing the apparatus. A method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate. An etching mask is formed on a metal layer formed on the insulating substrate and, using this etching mask, the metal layer is etched to form a constituent portion of the thin film transistor and protrusions. Only the etching mask is caused to reflow to cover exposed surface portions of the constituent portion of the thin film transistor and protrusions and near-by surface portions of the insulating substrate with the etching mask as the insulating substrate is partially exposed. Using the etching mask, recesses are formed in an exposed area of the insulating substrate. A reflector is formed on the protrusions and recesses.

FIELD OF THE INVENTION

[0001] This invention relates to a method for producing a liquid crystal display apparatus having a reflection type panel or a half-transmitting type panel. More particularly, it relates to a method for producing a liquid crystal display apparatus having an optimum display function with simplified processes.

BACKGROUND OF THE INVENTION

[0002] A liquid crystal display apparatus, employing active devices, such as thin-film transistors, features a thin thickness and a light weight, and is exploited as a high picture quality flat panel display. With the liquid crystal display apparatus, it is being contemplated to simplify the manufacturing process for realization of low production cost.

[0003] The liquid crystal display apparatus is being used as a display unit for a mobile terminal. The liquid crystal display apparatus used currently is predominantly a reflection type or semi-transmitting type liquid crystal display apparatus.

[0004] Of these, the reflection type liquid crystal display apparatus is designed so that a reflector provided within the apparatus reflects the light incident from outside. Reflected light is used as a display light source to render unnecessary backlight as a light source (see FIG. 3). As a result, the reflection type liquid crystal display apparatus lends itself more efficaciously to low power consumption, thinner thickness and lighter weight than the transmission type liquid crystal display apparatus.

[0005] On the other hand, the semi-transmission type liquid crystal display apparatus is designed to make efficacious display even on the occasion of the weak extraneous light. To this end, reflection display is made by exploiting reflected light, obtained on reflection of extraneous light by a reflector, at the same time as transmission display is made by exploiting backlight transmitted through an aperture (see 4 c in FIG. 2) provided in a portion of the reflector.

[0006] The basic structure of a liquid crystal display apparatus is made up by a liquid crystal of the TN (twisted nematic) system, a monolithic polarization plate system, an STN (super-twisted nematic) system, a GH (guest-host) system, a PDLC (polymer dispersion) system or a cholesteric system, a switching device, a reflector provided inside or outside the liquid crystal cell, and a transparent electrode.

[0007] A reflector, which is used as a pixel electrode, contributes to enhancement of the intensity of light scattered in an orientation perpendicular to a display picture surface with respect to the incident light entered with a large incident angle. With this reflector, a brighter display may be produced. By covering a passivation film, having a roughness formed on a surface, with a reflection film, to provide a reflection surface with a roughness, an optimum reflection characteristic may be achieved. As for a typical conventional method for forming a rough surface on a reflector, see for example the JP Patent Kokai JP-A10-319422.

[0008] A transparent electrode of ITO (indium tin oxide), used as a pixel electrode, may be formed as an uppermost layer, by layer separation from a drain layer, in order to improve the definition and aperture ratio of a display picture in a semi-transmission type liquid crystal display apparatus. The transparent electrode may also be formed on a surface of the reflector in order to prevent hillocks from being produced on the surface of the reflector formed of metal including Al.

[0009] The transparent electrode may also be used in a opening provided in the reflector in the semi-transmission type liquid crystal display apparatus, adapted for transmitting the backlight therethrough, so that the transparent electrode will operate as pixel electrodes. The transparent electrode is also sometimes used as wiring for electrically interconnecting a drain bus line and a drain electrode isolated therefrom.

[0010] In general, an active matrix substrate of a TN system is made up by a scanning line (termed a gate wiring or gate bus line) and a data line (termed a drain wiring or drain bus line), extending with orthogonal angles to each other, a reflector or a transparent electrode, formed in an area defined by these wirings, and thin-film transistors (TFTs) provided in the vicinity of the intersections of the gate and drain wirings. The active matrix substrate also includes a channel protection film on the TFT surface for guaranteeing the performance. On the TFTs, a reflector or a transparent electrode of this active matrix substrate, there is formed an orientation film for orienting the liquid crystal in a preset direction. The liquid crystal is sealed in a space defined by the active matrix substrate and by a counter substrate carrying another orientation film, a common electrode (transparent electrode) and a color filter, to complete the liquid crystal display apparatus.

[0011] By way of illustrating a conventional method for producing the liquid crystal display apparatus, the invention described in the JP Patent Kokai JP-A-10-319422 is now explained. FIGS. 81a-81 d and FIGS. 82e-82 g are cross-sectional views for schematically illustrating the processes for producing an active matrix substrate for a certain conventional reflection type liquid crystal display apparatus.

[0012] Referring first to FIG. 81a, in preparing an active matrix substrate, a gate electrode layer of, for example, Cr, is deposited on a transparent insulating substrate 101. Then, using a first mask, an exposed part of Cr is etched to form a gate bus line 102 and a gate electrode 103.

[0013] A gate insulating film 105, formed of SiN_(x), an a-Si(amorphous silicon) film 107 a and a n⁺ type a-Si film 107 b, which is to become an ohmic contact layer, are deposited in this order, as shown in FIG. 81b. Then, using a second mask, unneeded portions of the a-Si film 107 a and the n⁺ type a-Si film 107 b are selectively etched to form an island.

[0014] Then, referring to FIG. 81c, source/drain electrode layer of, for example, Cr, is then deposited and, using a third mask, unneeded portions of the source/drain electrode layer are selectively etched, for forming an opening in a channel area of the a-Si film 107 a and a preset wiring pattern, to form a source electrode 108, which is to become a signal line, a drain electrode 109 and a drain bus line 110.

[0015] Then, using the source electrode 108 and the drain electrode 109 as an etching mask, the n⁺ type a-Si film 107 b is etched to form an ohmic contact layer.

[0016] Then, referring to FIG. 81d, an organic insulating film 112 of, for example, polyimide, is deposited on the entire substrate surface. Then, using a fourth mask, a contact hole 113 for exposing a portion of the source electrode 108 and a contact hole 117 c for exposing a portion of the gate bus line 102 are formed.

[0017] Then, referring to FIG. 82e, a portion of the organic insulating film 112 is selectively removed, using a fifth mask, and a rough portion 112 b is formed, by heat treatment.

[0018] Referring to FIG. 82f, a layer of metal, such as Al, is deposited on the entire substrate surface and, using a sixth photo mask, the metal layer is selectively etched to form a reflector 104 b. This forms a reflector having a rough surface. The reflector 104 b is electrically connected to the source electrode 108 through the contact hole 113.

[0019] Finally, a transparent electrode layer of, for example, ITO (indium tin oxide) is deposited on the entire surface of the transparent insulating substrate 101, as shown in 82 g. Then, using a seventh photomask, a preset portion of the transparent electrode layer is removed to form a drain terminal 117 d connecting to the drain bus line 102 through the contact hole 117 c and a hillock inhibiting film 152, adapted for inhibiting generation of hillocks in the reflector 104 to complete the manufacture of the active matrix substrate. The hillock inhibiting film may also be a transparent electrode.

[0020] In the above-described active matrix substrate, the reflector which is to become the pixel electrode and the transparent electrode are not provided on the same layer as the source/drain electrode layer, but are insulated and separated from each other by an organic insulating film. Consequently, for insulation and separation of the transparent electrode layer and the drain electrode layer, these do not have to be separated from each other in the transverse direction relative to the normal line direction of the active matrix substrate, so that these can be extremely close to or overlapped with each other. As a result, the black matrix for shielding the uncontrolled backlight light rays, leaking from an interstice produced when the transparent electrode layer and the drain electrode layer are separated from each other in the transverse direction, can be rendered small and hence the aperture ratio can be meritoriously increased. For this reason, the transparent electrode layer and the drain electrode layer are insulated and separated from each other by an organic insulating film.

SUMMARY OF THE DISCLOSURE

[0021] In order to produce a liquid crystal display apparatus that is able to make bright high-quality display by using the conventional production method, it is necessary to form high performance transistors and high performance reflectors on one and the same insulating substrate, with the result that a large number of deposition processes, photolithography processes and etching processes are required.

[0022] In the conventional method for manufacturing the active matrix substrate, shown in FIGS. 81 and 82, there are required seven photolithography (PR) processes, namely, a PR process for forming a gate bus wiring and a gate electrode, a PR process for forming a contact layer and a semiconductor layer, a PR process for forming a source electrode, a drain electrode and a source/bus wiring, a PR process for forming the contact hole in the organic insulating film, a PR process for forming the rough surface of the organic insulating film, a PR process for forming the reflective plate and a PR process for forming the transparent electrode. These PR processes lead to increased production cost of the apparatus and hence to a high unit cost.

[0023] In light of the above, it has been desired to lower production cost through reduction in the number of PR steps and to realize high brightness and high quality display performance to enable the high brightness liquid crystal display apparatus at a low cost.

[0024] Accordingly, it is an object of the present invention to provide a liquid crystal display apparatus and a method for producing it, in which an optimum display performance of the liquid crystal display apparatus may be demonstrated even though the number of PR processes is diminished.

[0025] The above and other objects of the invention are satisfied, at least in part, in accordance with a first aspect of the present invention, by providing a method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing the first substrate, and a liquid crystal layer placed between the first substrate and the second substrate, in which the method includes a first step of forming an etching mask, patterned to a preset shape, on at least one of a metal layer, an insulating layer and a semiconductor layer, formed on the insulating substrate, a second step of etching at least one of the metal layer, insulating layer and the semiconductor layer, using the etching mask, to expose a portion of the insulating substrate and to form a constituent portion of the thin film transistor and a plurality of protrusions being separated from the constituent portion, a third step of causing only the etching mask to reflow to cover exposed part of the constituent portion of the thin film transistor and near-by surface portions of the insulating substrate with the etching mask and to cover exposed surfaces of the protrusions and near-by surface portions of the insulating substrate, while exposing surface portions of the insulating substrate between neighboring protrusions, a fourth step of etching said insulating substrate, following said third step, using said etching mask, to form one or more recesses in exposed areas of said insulating substrate, and a fifth step of selectively forming a reflector having a rough surface on a rough surface formed at least by said protrusions and recesses.

[0026] In the method for producing the liquid crystal display apparatus in accordance with the present invention, in case a metal layer and an insulation layer are formed in this order on the insulating substrate, it is preferred to etch the insulating layer in the second step, using the etching mask, to expose portions of the metal layer, and to stop the contact hole by the etching mask by reflow of the etching mask in the third step. When the insulating substrate is a glass substrate and the etching liquid is HF, and the metal layer is exposed from the contact hole, there is a risk of HF permeating through the metal layer to etch the underlying glass substrate.

[0027] The method for producing a liquid crystal display apparatus in accordance with the present invention, desirably includes a sixth step following the fourth step and previous to the fifth step, with the sixth step forming another insulating layer having a rough surface on the rough surface at least formed by the protrusions and recesses. It is because this step renders it possible to adjust the rounding of the irregularities when the surface roughness of the rough surface formed by the protrusions and recesses is excessive, that is when the rough surface is square-shaped.

[0028] In accordance with a second aspect of the present invention, there is provided a method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing the first substrate, and a liquid crystal layer placed between the first substrate and the second substrate, in which the method includes a first step of forming a metal layer on the insulating substrate, and subsequently etching the metal layer using a first etching mask to expose a portion of the insulating substrate and to form a gate electrode, a second step of causing only the etching mask to reflow to cover the exposed surface of the gate insulating electrode and near-by surface portions of the insulating substrate with the etching mask and to cover the exposed surface portions of the protrusions and near-by surface portions of the insulating substrate with the etching mask, a third step of etching the insulating substrate using the etching mask to form one or more recesses in an exposed area of the insulating substrate and a fourth step of selectively forming a reflector having a rough surface on the rough surface of the insulating layer.

[0029] In accordance with a third aspect of the present invention, there is provided a method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing the first substrate, and a liquid crystal layer placed between the first substrate and the second substrate, in which the method includes a first step of etching the metal layer, using a first etching mask, following the formation of a metal layer on the insulating substrate, to expose a portion of the insulating substrate and to form a gate electrode, a second step of forming an insulating layer on the insulating substrate including the gate electrode and subsequently etching the insulating layer, using a second etching mask, to expose portions of the insulating substrate while forming a gate insulating film and a plurality of protrusions separated from the gate insulating films, a third step of causing only the etching mask to reflow to cover exposed portions of the gate insulating films and near-by surface portions of the insulating substrate with the etching mask and to cover exposed surfaces of the protrusions and near-by surface portions of the insulating substrate, while exposing the surface portions of the insulating substrate between neighboring protrusions, a fourth step of etching the insulating substrate, following the third step, using the etching mask, to form one or more recesses in exposed areas of the insulating substrate and a fifth step of selectively forming a reflector having a rough surface on the rough surface formed at least by the protrusions and recesses.

[0030] In the method for producing a liquid crystal display apparatus, in accordance with the present invention, a sixth step of forming a semiconductor layer on the insulating layer and of subsequently etching the semiconductor layer, using a third etching mask, to form an island above the gate electrode, is preferably provided following formation of the insulating layer and prior to using the second etching mask in the second step.

[0031] In the method for producing a liquid crystal display apparatus, in accordance with the present invention, the reflector formed in the second step is directly arranged on the rough surface formed by the protrusions and recesses. It is because surface roughness of the rough surface formed by the protrusions and recesses can be prevented from being decreased.

[0032] In the method for producing a liquid crystal display apparatus, in accordance with the present invention, the reflector is of a laminated structure comprised of a lower Cr layer and an upper Al/Nd layer. The source electrode and the drain electrode of the laminated structure are selectively formed when the reflector is formed in the fifth step. A contact hole for partially exposing the Cr layer of the source electrode is formed in an other insulation layer formed on the insulating layer comprised of the reflector, source electrode and the drain electrode, and in the Al/Nd layer, after forming the other insulating layer. A transparent electrode layer electrically connecting to the source electrode through the contact hole is selectively formed on the other insulating layer. It is because optimum electrical conductivity may be maintained between the source electrode and the transparent electrode layer, such as ITO, as hillocks are prevented from being produced on the surface of the Al/Nd layer in the reflector.

[0033] In accordance with a fourth aspect of the present invention, there is provided a method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing the first substrate, and a liquid crystal layer placed between the first substrate and the second substrate, in which the method includes a first step of forming a first metal layer on the insulating substrate and subsequently etching the first metal layer, using a first etching mask, to expose a portion of the insulating substrate and to form a gate electrode, a second step of forming a first insulating layer and a semiconductor layer in this order on the insulating substrate including the gate electrode and of subsequently etching the semiconductor layer using a second etching mask to form an island above the gate electrode, a third step of forming a second metal layer on the first insulating layer including the island and of subsequently etching the second metal layer using a third etching mask to form the source electrode and the drain electrode, a fourth step of forming a second insulating layer on the first insulating layer including the source electrode and the drain electrode and of subsequently etching the second insulating layer and the first insulating layer, using a fourth etching mask, to expose a portion of the insulating substrate and to form a plurality of protrusions, a fifth step of causing only the fourth etching mask to reflow following the fourth step to cover exposed surface portions of the first and second insulating layers and near-by surface portions of the insulating substrate with the fourth etching mask and to cover exposed surface portions of the protrusions and near-by surface portions of the insulating substrate with the fourth etching mask while exposing surface portions of the insulating substrate lying between neighboring protrusions, a sixth step of etching the insulating substrate, using the fourth etching mask, following the fifth step, to selectively form one or more recesses in an exposed area of the insulating substrate, and a seventh step of selectively forming a reflector which has a rough surface on the rough surface formed at least by the protrusions and recesses.

[0034] In accordance with a fifth aspect of the present invention, there is provided a method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on a predominantly planar insulating substrate, a second substrate having a transparent electrode and mounted facing the first substrate, and a liquid crystal layer placed between the first substrate and the second substrate, in which the method includes a first step of etching the planar insulating substrate, using a first etching mask, to selectively form a rough surface in a preset area of the insulating substrate, and a second step of etching the metal layer, using a second etching mask, for selectively forming a gate electrode on a planar area of the insulating substrate, and for selectively forming a reflector having a rough surface overlying a rough surface of the insulating substrate in register herewith and in isolation from the gate electrode.

[0035] In accordance with a sixth aspect of the present invention, there is provided a method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing the first substrate, and a liquid crystal layer placed between the first substrate and the second substrate, in which the method includes a first step of forming a first metal layer on the insulating substrate and subsequently etching the first metal layer using a first etching mask, to expose a portion of the insulating substrate, and to form a gate electrode, a plurality of protrusions separated therefrom, and a wiring isolated from the gate electrode and the protrusions, a second step of causing only the first etching mask to reflow to cover exposed surfaces of the gate electrode and the wiring and near-by surface portions of the insulating substrate with the first etching mask and to cover exposed surfaces of the protrusions and near-by surface portions of the insulating substrate with the first etching mask, a third step of etching the insulating substrate, using the first etching mask, after the second step, to form one or more recesses in the exposed area of the insulating substrate, a fourth step of etching the semiconductor layer, using a second etching mask, after forming a first insulating film and a semiconductor layer on the insulating substrate, including the gate electrode, the protrusions and the wiring, to form an island above the gate electrode, a fifth step of etching the first insulating layer, using a third etching mask, to expose a portion of the wiring to form a first contact hole, a sixth step of etching a second metal layer, using a fourth etching mask, after forming the second metal layer on the first insulating layer, including the island, to form a source electrode, a drain electrode and a reflector, to electrically connect the source electrode through the first contact hole with the wiring, a seventh step of forming, after forming a second insulating layer on the first insulating layer including the source electrode, drain electrode and the reflector, a second contact hole in the second insulating layer and in the first insulating layer, using a fifth etching mask, for exposing a portion of the wiring, and an eighth step of selectively forming a transparent electrode layer on the second insulating layer for electrically connecting to the wiring through the second contact hole. It is because it is possible to prevent the electrical field applied to the liquid crystal from being reduced when the transparent electrode is in the uppermost layer, and because the source electrode and the transparent electrode can be electrically interconnected through ha wiring to prevent shorting across the drain electrode and the transparent electrode.

[0036] In accordance with a seventh aspect of the present invention, there is provided a method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing the first substrate, and a liquid crystal layer placed between the first substrate and the second substrate, in which the method includes a first step of forming a first metal layer on the insulating substrate and subsequently etching the first metal layer, using a first etching mask, to expose a portion of the insulating substrate, and to form a gate electrode and a wiring separated from the gate electrode, a second step of forming a first insulating layer and a semiconductor layer in this order on the insulating substrate including the gate electrode and the wiring, and subsequently etching the semiconductor layer, using a second etching mask, to form an island above the gate electrode, a third step of etching the first insulating layer, using a third etching mask, to form a first contact hole which exposes a portion of the wiring, of exposing a portion of the insulating substrate and of forming a plurality of protrusions, a fourth step of causing only the third etching mask to reflow to cover the exposed surface portions of the first insulating layer and near-by surface portions of the insulating substrate with the third etching mask, to stop up the first contact hole with the third etching mask and to cover the exposed surface portions of the protrusions and near-by surface portions of the insulating substrate with the third etching mask while exposing surface portions of the insulating substrate located between neighboring protrusions and nearby surface portions of the insulating substrate, a fifth step of etching the insulating substrate, after the fourth step, using the third etching mask, to form one or more recesses in an exposed area of the insulating substrate, a sixth step of forming a second metal layer on the first insulating layer including the island, on the protrusions and on the recesses, and subsequently etching the second metal layer, using a fourth etching mask, to form a source electrode, a drain electrode and a reflector, to connect the source electrode electrically to the wiring through the first contact hole, a seventh step of forming a second insulating layer on the first insulating layer including the source electrode, drain electrode and the reflector, and subsequently forming a second contact hole, which exposes a portion of the wiring to the second insulating layer and the first insulating layer, using a fifth etching mask, and an eighth step of selectively forming a transparent electrode layer on sad second insulating layer for electrically connecting to the wiring through the second contact hole.

[0037] In the method for producing a liquid crystal display apparatus, the etching mask is preferably a photoresist.

[0038] In the method for producing a liquid crystal display apparatus, the reflector has an opening in a preset area in its rough surface.

[0039] Still other objects and advantages of the present invention will become readily apparent to those skilled in this art from the following detailed description in conjunction with the accompanying drawings wherein only the preferred embodiments of the invention are shown and described, simply by way of illustration of the best mode contemplated of carrying out this invention. As will be realized, the invention is capable of other and different embodiments, and its several details are capable of modifications in various obvious respects, all without departing from the invention. Accordingly, the drawing and description are to be regarded as illustrative in nature, and not as restrictive.

BRIEF DESCRIPTION OF THE DRAWINGS

[0040]FIG. 1 is a block diagram schematically showing the structure of a liquid crystal display apparatus according to a first embodiment of the present invention.

[0041]FIG. 2 is a partial cross-sectional view schematically showing the structure of a display unit in a semi-transmission type liquid crystal display apparatus according to the first embodiment of the present invention.

[0042]FIG. 3 is a partial cross-sectional view schematically showing the structure of a display unit in a reflection type liquid crystal display apparatus according to the first embodiment of the present invention.

[0043]FIG. 4 is a plan view schematically showing the structure of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0044]FIG. 5 is a first plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0045]FIG. 6 is a second plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0046]FIG. 7 is a third plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0047]FIG. 8 is a fourth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0048]FIG. 9 is a fifth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0049]FIG. 10 is a sixth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0050]FIGS. 11a-11 f are cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0051]FIGS. 12a-12 f are views along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0052]FIGS. 13a-13 f are cross-sectional views along line C-C′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0053]FIGS. 14a-14 f are cross-sectional views along line D-D′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0054]FIGS. 14a-15 f are cross-sectional views along line E-E′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention.

[0055]FIG. 16 is a first plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0056]FIG. 17 is a second plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0057]FIG. 18 is a third plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0058]FIG. 19 is a fourth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0059]FIG. 20 is a fifth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0060]FIG. 21 is a sixth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0061]FIG. 22 is a seventh plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0062]FIGS. 23a-23 d are first cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0063]FIGS. 24e-24 h second cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0064]FIGS. 25a-25 d are first cross-sectional views along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0065]FIGS. 26e-26 h are second cross-sectional views along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0066]FIGS. 27a-27 d are first cross-sectional views along line C-C′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0067]FIGS. 28e-28 h are second cross-sectional views along line C-C′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0068]FIGS. 29a-29 d are first cross-sectional view along line D-D′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0069]FIGS. 30e-30 h are second cross-sectional views along line D-D′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0070]FIGS. 31a-31 d are first cross-sectional views along line E-E′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0071]FIGS. 32e-32 h are second cross-sectional views along line E-E′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the second embodiment of the present invention.

[0072]FIG. 33 is a first plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to a third embodiment of the present invention.

[0073]FIG. 34 is a second plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0074]FIG. 35 is a third plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0075]FIG. 36 is a fourth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0076]FIG. 37 is a fifth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0077]FIG. 38 is a sixth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0078]FIGS. 39a-39 d are first cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0079]FIGS. 40e-40 g are second cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0080]FIGS. 41a-41 d are first cross-sectional views along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0081]FIGS. 42e-42 g are second cross-sectional views along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0082]FIGS. 43a-43 g are cross-sectional views along line C-C′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0083]FIGS. 44a-44 g are cross-sectional views along line D-D′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0084]FIGS. 45a-45 g are second cross-sectional views along line E-E′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the third embodiment of the present invention.

[0085]FIG. 46 is a first plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to a fourth embodiment of the present invention.

[0086]FIG. 47 is a second plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0087]FIG. 48 is a third plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0088]FIG. 49 is a fourth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0089]FIG. 50 is a fifth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0090]FIG. 51 is a sixth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0091]FIG. 52 is a seventh plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0092]FIGS. 53a-53 d are first cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to a fourth embodiment of the present invention.

[0093]FIGS. 54e-54 h are second cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0094]FIGS. 55a-55 d are first cross-sectional views along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0095]FIGS. 56a-56 h are second cross-sectional views along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0096]FIGS. 57a-57 d are first cross-sectional views along line C-C′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0097]FIGS. 58e-58 h are second cross-sectional views along line C-C′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0098]FIGS. 59a-59 d are first cross-sectional views along line D-D′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0099]FIGS. 60e-60 h are second cross-sectional views along line D-D′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0100]FIGS. 61a-61 d are first cross-sectional views along line E-E′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0101]FIGS. 62e-62 h are second cross-sectional views along line E-E′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0102]FIG. 63 is a first plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to a fifth embodiment of the present invention.

[0103]FIG. 64 is a second plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment of the present invention.

[0104]FIG. 65 is a third plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0105]FIG. 66 is a fourth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0106]FIG. 67 is a fifth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0107]FIG. 68 is a sixth plan view schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0108]FIGS. 69a-69 d are first cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0109]FIGS. 70e-70 h are second cross-sectional views along line A-A′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0110]FIGS. 71a-71 d are first cross-sectional view along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0111]FIGS. 72e-72 h are second cross-sectional views along line B-B′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0112]FIGS. 73a-73 d are first cross-sectional views along line C-C′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0113]FIGS. 74e-74 h are second cross-sectional views along line C-C′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0114]FIGS. 75a-75 d are first cross-sectional views along line D-D′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0115]FIGS. 76e-76 h are second cross-sectional views along line D-D′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0116]FIGS. 77a-77 d are first cross-sectional views along line E-E′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0117]FIGS. 78e-78 h are second cross-sectional views along line E-E′ schematically showing the production process of the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment of the present invention.

[0118]FIGS. 79a-79 d are first cross-sectional views schematically showing the production process of an active matrix substrate in the liquid crystal display apparatus according to a sixth embodiment of the present invention.

[0119]FIGS. 80e-80 h are second cross-sectional views schematically showing the production process of an active matrix substrate in the liquid crystal display apparatus according to the sixth embodiment of the present invention.

[0120]FIGS. 81a-81 d are first cross-sectional views schematically showing the production process of an active matrix substrate for a conventional reflection type liquid crystal display apparatus.

[0121]FIGS. 82e-82 g are second cross-sectional views schematically showing the production process of an active matrix substrate for the conventional reflection type liquid crystal display apparatus.

PREFERRED EMBODIMENTS OF THE INVENTION

[0122] Preferred embodiments of the present invention will now be described in the below. According to the present invention, a method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing the first substrate, and a liquid crystal layer placed between the first substrate and the second substrate includes a first step of forming an etching mask (24 of FIG. 23), patterned to a preset shape, on at least one of a metal layer (3 a, 25, and 26 of FIG. 23), an insulating layer and a semiconductor layer, formed on the insulating substrate (1 of FIG. 23), a second step (FIG. 23a) of etching at least one of the metal layer, insulating layer and the semiconductor layer, using the etching mask, to expose a portion of the insulating substrate under forming constituent portion (3 a of FIG. 23) of the thin film transistor and a plurality of protrusions (26 of FIG. 23) being separated from the constituent portion, a third step (FIG. 23b) of causing only the etching mask to reflow to cover exposed portions of the constituent portion of the thin film transistor and near-by surface portions of the insulating substrate with the etching mask and to cover exposed surfaces of the protrusions and near-by surface portions of the insulating substrate under exposing surface portions of the insulating substrate between neighboring protrusions, a fourth step (FIG. 23c) of etching the insulating substrate, following the third step, using the etching mask, to form one or more recesses (1 a and 1 b of FIG. 23) in exposed areas of the insulating substrate, and a fifth step (FIG. 24f) of selectively forming a reflector (4 a and 4 b of FIG. 24) having a rough surface on a rough surface formed at least by the protrusions and recesses. Thus, with the use of a sole etching mask, the constituent portion of the thin film transistor, such as a gate electrode or a gate insulating film, may be formed at the same time as a rough surface presenting pronounced inundations are produced.

[0123] For illustrating the above described various aspects of the present invention, certain embodiments of the invention are now explained in detail with reference to the drawings.

[0124]FIG. 1 is a block diagram schematically illustrating the structure of the liquid crystal display apparatus according to the first embodiment of the present invention. FIG. 2 is a partial cross-sectional view schematically illustrating the structure of a display unit in the semi-transmission type liquid crystal display apparatus according to the first embodiment of the present invention. FIG. 3 is a partial cross-sectional view schematically illustrating the structure of a display unit in the reflection type liquid crystal display apparatus according to the first embodiment of the present invention. FIG. 4 is a plan view schematically illustrating the structure of an active matrix in the liquid crystal display apparatus according to the first embodiment of the present invention. FIGS. 5 to 10 are plan views schematically illustrating the production process for the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention. FIG. 11a to FIG. 15f are cross-sectional views schematically illustrating the production process for the active matrix substrate in the liquid crystal display apparatus according to the first embodiment of the present invention, taken along lines A-A′, B-B′, C-C′, D-D′ and E-E′, respectively.

[0125] Referring to FIG. 1, the liquid crystal display apparatus includes a picture processing circuit, a control circuit, and a display voltage generating circuit, a drain driver(termed also as a data driver), a gate driver(termed also as a scanning line driver) and a display panel.

[0126] The picture processing circuit executes pre-set calculations, based on the picture information, and sends the calculated picture processing signals to the control circuit.

[0127] The control circuit performs fine position adjustment, such as alignment of the drain driver and the gate driver, based on the picture processing signals, as received, while controlling the voltage generated in a display voltage generating circuit.

[0128] The display voltage generating circuit sends a preset voltage to each of the common terminals in the drain driver, gate driver and in the display panel, under the control from the control circuit.

[0129] Moreover, the drain driver drives the drain bus lines on the active matrix substrate in the display panel, through the drain terminal, under control from the control circuit.

[0130] The gate driver drives the gate bus lines on the active matrix substrate in the display panel through the gate terminal under control from the control circuit.

[0131] As for the module mounting on the display panel, known techniques such as TCP (tape carrier package), COG (chip on glass) or COF (chip on flexible printed circuit board) are used.

[0132] Referring to FIG. 2, the display panel comprises, in the case of the semi-transmission type liquid crystal display apparatus, an orientation film 16 on the entire surface towards a transparent electrode 14 of an active matrix substrate 15 which includes a reflector 4 provided with an opening 4 c. The display panel also comprises, on the entire surface towards the insulating substrate of the active matrix substrate 15, a phase difference plate 31, a polarization plate 32 and a backlight 33, in this order, looking from the side insulating substrate. A liquid crystal layer 50 is interposed between an orientation film 41 provided on an opposite side substrate 40 and an orientation film 16 provided on the active matrix substrate 15. The opposite side substrate 40 comprises the orientation film 41, an opposite side transparent common electrode 42, a resin protective film 43, a color filter 44, an opposite side transparent insulating substrate 45, a phase difference plate 46 and a polarization plate 47, stacked in this order from the side liquid crystal layer.

[0133] Referring to FIG. 3, showing a reflection type liquid crystal display apparatus, there is provided no backlight on the side insulating substrate of the active matrix substrate 15 provided with the reflector 4 not having the opening. The arrangement of the orientation film 16, liquid crystal layer 50 and the opposite side substrate 40 is not changed from that in the case of the semi-transmission type liquid crystal display apparatus.

[0134] Referring to FIG. 4, the active matrix substrate 15 includes a driving element for each pixel or dot in the matrix, and drives the liquid crystal by switching the driving elements.

[0135] Referring to FIGS. 10 and 11, the active matrix substrate according to the present embodiment is constructed as follows:

[0136] In an area of a planar surface of an insulating substrate 1 of, for example, glass, plastics or poly-carbonate, having a rough surface 1 a in a preset area, plural gate bus lines 2 made up of, for example, a Cr, Ta, Mo, Ti or Cr/Al are arranged parallel to one another. A gate electrode 3 is branched from each gate bus line 2. In the case of the reflection type apparatus, the insulating substrate 1 need not be transparent. The gate bus line 2 operates as a scanning line. A reflector 4 (4 a and 4 b) made up of, for example, Cr, Ta, Mo, Ti or Cr/Al is provided in the area of the insulating substrate 1 provided with the rough surface 1 a.

[0137] The reflector 4 is isolated from the gate bus line 2. The surface of the reflector 4 is rough as is the rough surface 1 a of the insulating substrate 1, and extends along the rough surface 1 a. The maximum height of the surface roughness is on the order of 2 to 3 μm, with the spacing between adjoining crests being on the order of tens of μm. In the case of the semi-transmission type liquid crystal display apparatus, an aperture 4 c is provided in a portion of the rough surface area of the reflector 4 for transmitting the light emitted from a backlight. In the case of the reflection type liquid crystal display apparatus, no aperture is provided in the rough surface in the reflector 4. Although the protrusions and dents of the rough surface shown in the drawings may be seen to be sharp, these protrusions and dents are actually rounded smoothly.

[0138] A gate insulating film 5 of, for example, SiN_(x) or SiO_(x), is formed on the insulating substrate 1 provided with the gate electrode 3 and the reflector 4. The gate insulating film 5 includes a contact hole 6 for exposing a portion of the reflector 4, and has on its surface a rough surface lying on the rough surface of the reflector 4.

[0139] On the gate insulating film overlying the gate electrode 3, there is formed an island 7, made up by a semiconductor layer 7 a, formed e.g., of amorphous silicon (a-Si) or polycrystalline silicon, and a contact electrode 7 b of n⁺ type a-Si on each end of the semiconductor layer.

[0140] On one end of the island 7, there is formed a source electrode 8 (8 a) of, for example, Cr, Ta, Mo, Ti or Cr/Al, whereas, on the opposite side thereof, there is formed a drain electrode 9 (9 a) of, for example, Cr, Ta, Mo, Ti or Cr/Al. The drain electrode 9 is branched from the drain bus line 10 (10 a), which intersects the gate bus line 2 via gate insulating film 5. The drain bus line 10 operates as a signal line and is formed of metal, as is the drain electrode 9.

[0141] The gate electrode 3, gate-insulating film 5, island 7, source electrode 8 and the drain electrode 9 compose a thin-film transistor (TFT) 11. This TFT 11 operates as a switching device.

[0142] On the entire surface of the substrate including the gate bus line 2, drain bus line 10 and the TFT 11, there is formed a passivation film 12 of, for example, SiN_(x) or SiO_(x). The passivation film 12 includes a first contact hole 6 in a region corresponding to the contact hole in the gate insulating film 5, a second contact hole 13, at a preset position on the source electrode 8, for exposing the source electrode 8, and a rough surface, in an area of the rough surface of the gate insulating film 5, for extending along this rough surface of the gate insulating film.

[0143] In an area on the passivation film 12 having the rough surface, there is provided a transparent electrode 14 formed of, for example, ITO (indium tin oxide) or IZO (indium zinc oxide). The transparent electrode 14 serves to connect electrically the reflector 4 to the source electrode 8 through the first contact hole 6 and the second contact hole 13. The transparent electrode 1 operates, together with the reflector 4, as pixel electrodes.

[0144] At a corner of the insulating substrate 1, there are formed a common terminal unit 19, a common device unit 20 and a common bus line 21 for applying the common potential to the gate bus line 2, drain bus line 10 of the active matrix substrate 15 and to the opposite side transparent common electrode 42 of the opposite side substrate 40 of FIGS. 2 and 3. Although not shown, a storage capacitor may be formed between each TFT 11 and the neighboring gate bus line 2.

[0145] The process for producing the active matrix substrate according to the first embodiment is now explained.

[0146] First referring to FIGS. 5, 11a, 12 a, 13 a, 14 a and 15 a, a first mask, not shown, is formed on a planar insulating substrate 1 of, for example, glass, by a photolithography technique. A rough surface 1 a then is formed on the insulating substrate 1 having a flat surface, such as a glass substrate, by a photolithography technique. Then, by e.g., wet etching, employing HF (hydrofluoric acid), sand-blasting, or dry etching, employing CF₄ or O₂, a rough surface 1 a is formed in a preset area of the insulating substrate 1. The resulting product is washed and the first mask is removed.

[0147] The wet etching of the glass substrate is meritorious in that the back surface of the substrate is simultaneously etched to thereby reduce the substrate thickness.

[0148] Then, referring to FIGS. 6, 11b, 12 b, 13 b, 14 b and 15 b, underlying metal layers 2 a, 3 a, 4 a and 17 a of, for example, Cr, Ti or Mo (referred to below as ‘Cr’), and overlying metal layers 2 b, 3 b, 4 b and 17 b of, for example, Al (referred to below as ‘Al/Nd’ are deposited in this order on the entire surface of the insulating substrate 1 to form a gate electrode layer, not shown.

[0149] It is noted that the gate electrode layer is deposited, using, for example, a sputtering method, so that the total film thickness of the underlying metal Cr and the overlying metal Al/Nd will be on he order of 100 to 200 nm.

[0150] Then, referring to FIGS. 6, 11b, 12 b, 13 b, 14 b and 15 b, a second mask, not shown, is formed by the photolithography technique on the gate electrode layer. An unneeded electrode layer then is removed by dry etching or wet etching. The second mask then is removed. This forms the gate electrode 3, the gate bus line 2, underlying metal layers 17 a and 17 b of the gate terminal unit, reflector 4, an underlying metal layer 19 a, a common bus line 21 for the drain and gate electrodes 20 d, and 20 e for the common device unit.

[0151] The underlying metal layers 17 a and 17 b are connected to the gate bus line 2. In the case of the reflection type apparatus, no aperture is provided in the reflector 4, whereas, in the semi-transmission type apparatus, an aperture 4 c is provided in the reflector 4. The underlying metal layer 19 a for the common terminal unit is connected to the common bus line 21 for the drain. The gate electrode 20 d for the common device unit is connected to the common bus line 21 or to the gate bus line 2. The gate electrode 20 e for the common device unit is separated from the common bus line 21 for the drain and from the gate bus line 2.

[0152] Then, referring to FIGS. 7, 11c, 12 c, 13 c, 14 c and 15 c, the gate insulating film 5, a-Si layer 7 a which is to become a semiconductor layer, and a n⁺ type a-Si layer 7 b, which is to become a contact electrode, are sequentially formed on the entire surface of the substrate provided with the gate electrode 3, gate bus line 2, underlying metal layers 17 a and 17 b for the gate terminal unit, reflector 4, underlying metal layer 19 a for the common terminal unit, common bus line 21 for the drain and the gate electrodes 20 d, and 20 e for the common device unit. The semiconductor layer and the contact electrode form islands 7 and 20 f.

[0153] The gate insulating film 5 is formed by for example a plasma CVD method to a film thickness of the order of 300 to 500 nm. For forming the islands 7, and 20 f, a-Si, for example, is formed to a film having a film thickness on the order of 150 to 400 nm, by a plasma CVD method, while n⁺ a-Si is formed to a film having a film thickness on the order of 20 to 60 nm, by a plasma CVD method.

[0154] In forming the n⁺ type a-Si layer 7 b, a substrate on which film deposition has been completed up to the a-Si layer 7 a is held in a PH₃ plasma atmosphere and phosphorus(P) is diffused into the a-Si layer 7 a to form a n⁺ layer, as a surface layer, in order to form an ohmic contact to the a-Si layer 7 a. The processing conditions for achieving this include using a plasma CVD system, supplying the PH₃/H₂ (0.5% PH₃) gas at 1000 sccm at a temperature of 300° C. and processing for five minutes under a pressure of 200 Pa and an RF power of 0.1 W/cm².

[0155] Then, referring to FIGS. 7, 11c, 12 c, 13 c, 14 c and 15 c, a third mask, not shown, is formed by the photolithography technique on the n⁺ type a-Si layer 7 b. Then, by e.g., dry etching, the unneeded a-Si layer 7 a and unneeded n⁺ type a-Si layer 7 b are removed and the third mask then is removed. This forms the dry islands 7, 20 f. The island 7 is formed above the gate electrode 3 adapted for driving a liquid crystal. The island 20 f is formed above the gate electrodes 20 d for the common device, the gate electrodes 20 e for the common device unit, gate electrodes 20 d for the common device unit and the gate electrodes 20 e for the common device unit.

[0156] Then, referring to FIGS. 8, 11d, 12 d, 13 d, 14 d and 15 d, metal layers 8 a, 9 a, 10 a, 18 a, 20 a and 22 a are deposited on the entire surface of the substrate, provided with the gate electrode 3, gate bus line 2, underlying metal layers 17 a and 17 b for the gate terminal unit, reflector 4, underlying metal layer 19 a for the common terminal unit, common bus line 21 for the drain, gate electrodes 20 d, and 20 e for the common device unit, and the islands 7, and 20 f, to a film thickness of 100 to 200 nm, by e.g., a sputtering method.

[0157] Then, referring to FIGS. 8, 11d, 12 d, 13 d, 14 d and 15 d, a fourth mask, not shown, is formed, by a photolithography technique, on the metal layers 8 a, 9 a, 1 a, 18 a, 20 a and 22 a. Then, unneeded metal is removed by dry etching. This forms a source electrode 8, a drain electrode 9, a drain bus line 10, an underlying metal 18 a for the drain terminal unit, a common bus line 22 for the gate, and plural source/drain electrodes 20 a for the common device unit. Part of plural source/drain electrodes 20 a for the common device unit is connected to the drain bus line 10 and to the common bus line 22 a for the gate.

[0158] The n⁺ type a-Si layer 7 b then is etched, using the source electrode 8 a, drain electrode 9 a and the fourth mask, as etching masks. The fourth etching mask then is removed. This forms an ohmic contact layer.

[0159] Then, referring to FIGS. 9, 11e, 12 e, 13 e, 14 e and 15 e, a passivation film 12 of, for example, SiN_(x), is formed to a film thickness of 100 to 500 nm, by the plasma CVD method, on the entire surface of the substrate provided with the gate electrode 3, gate bus line 2, underlying metal layers 17 a and 17 b for the gate terminal unit, reflector 4, underlying metal layer 19 a for the common terminal unit, common bus line 21 for the drain, gate electrodes 20 d and 20 e for the common device unit, islands 7, and 20 f, source electrode 8, drain electrode 9, drain bus line 10, underlying metal 18 a for the drain terminal unit, common bus line 22 a for the gate, and plural source/drain electrodes 20 a for the common device unit.

[0160] As the material for the passivation film 12, such a material is to be selected and used which will give a sufficiently large etching selection ratio for the a-Si a7 and the gate insulating film 5, in order to form the contact holes 6, 13 and the like in the subsequent process steps.

[0161] Then, referring to FIGS. 9, 11e, 12 e, 13 e, 14 e and 15 e, a fifth mask, not shown, is formed, by a photolithography technique, on the passivation film 12. Then, excess portions of the passivation film 12, gate insulating film 5 or the Al/Nd layers 2 b, 4 b, 17 b, 19 a and 21 b, lying in areas which later become contact holes, are removed by, for example, dry etching, until part of the Cr layers 2 a, 4 a, 8 a, 10 a, 17 a, 18 a, 19 a, 20 a, 20 d, 20 e, 21 a and 22 a is exposed. The fifth mask then is removed. With this process, contact holes 6, 13, 17 c, 18 c, 19 b, 20 c, 21 c and 22 c are formed.

[0162] It is noted that the contact hole 6 exposes part of the Cr layer 4 a of the reflector. The contact hole 13 exposes part of the source electrode (Cr layer) 8 a. The contact hole 17 c exposes part of the Cr layer 17 a of the gate terminal unit. The contact hole 18 c exposes part of the Cr layer 18 a of the drain terminal unit. The contact hole 19 b exposes part of the Cr layer 19 a of the common terminal unit. The contact hole 20 c-expose part of the Cr layers 2 a, 20 a, 20 d, 20 e, 21 a, and 22 a of the common device unit. The contact hole 21 c exposes part of the Cr layer 21 a for the common bus line for the drain. The contact hole 22 c exposes part of the Cr layer 22 a of the common bus line for the gate.

[0163] The reason why the Al/Nd layers 2 b, 4 b, 17 b, 19 a and 21 b for the contact holes 6, 17 c, 19 b and part of 20 c, 20 e and 21 r are removed is that, without this removal, the electrical conductivity of Al/Nd with the ITO which later becomes the pixels in the subsequent process is not good.

[0164] Then, referring to FIGS. 10, 11f, 12 f, 13 f, 14 f and 15 f, transparent electrode layers 14, 17 d, 18 d, 19 c, 20 g and 23 of, for example, ITO, are deposited, by sputtering, on the entire surface substrate provided with the passivation film 12, to a film thickness of the order of 30 to 100 nm.

[0165] Finally, referring to FIGS. 10, 11f, 12 f, 13 f, 14 f and 15 f, a sixth mask, not shown, is formed by a photolithography technique on the transparent electrode layers 14, 17 d, 18 d, 19 c, 20 g and 23. Then, unneeded portions of the transparent electrode layers are removed by wet etching (oxalic acid, aqua regia, ferric chloride plus hydrochloric acid). The sixth mask then is removed. This forms a transparent electrode 14 which later becomes a pixel electrode, a terminal 17 d of the gate terminal unit, a terminal 18 d of the drain terminal unit, a terminal 19 c of the common terminal unit, a wiring 20 g of the common terminal unit and a wiring 23 across the common bus lines 21 and 22.

[0166] It is noted that the transparent electrode 14 electrically connects the source electrode 8 and the reflector 4 through the contact holes 6 and 13 (see FIGS. 7 and 9). The terminal 17 d of the gate terminal unit, the terminal 18 d of the drain terminal unit and the terminal 19 c of the common terminal unit connect to the Cr layers 17 a, 18 a and 19 a of the respective parts through contact holes 17 c, 18 c and 19 b of the respective parts. Through contact holes of an optional combination, the wiring 20 f of the common device unit electrically connects the gate bus line 2 to the source/drain electrode 20 a of the common device unit, while connecting the common bus line 22 to the gate electrode 20 e of the common device unit, connecting the common bus line 21 to the source/drain electrode 20 a of the common device unit and connecting the drain bus line 10 to the gate electrode 20 e of the common device unit. The wiring 23 across the common bus lines 21, and 22 electrically connects the common bus lines 21, 22 across the contact holes 21 c, and 22 c.

[0167] If the transparent electrode 14, as the pixel electrode, is formed on the uppermost layer of the substrate, there is derived a merit that the electrical field can be applied directly to the liquid crystal without separation by e.g., an insulating film. In light of above, the transparent electrode 14 is desirably provided as an uppermost layer of the substrate, even in the case of the reflection type apparatus.

[0168] The above process may produce the active matrix substrate, constructed as shown in FIG. 11. Thus, with the method for manufacturing the active matrix substrate according to the first embodiment, described above, a reflection type or semi-transparent type active matrix substrate of optimum display performance, presenting irregularities on its reflector, can be formed using only six masks, so that the manufacturing process can be simplified at least by one PR as compared to the customary manufacturing process.

[0169] The second embodiment of the present invention is now explained with reference to the drawings. FIGS. 16 to 22 are schematic plan views showing he manufacturing process of the active matrix substrate for the liquid crystal display apparatus according to the second embodiment of the present invention. FIGS. 23 to 32 are schematic cross-sectional views showing the manufacturing process of the active matrix substrate for the liquid crystal display apparatus according to the second embodiment of the present invention. In FIGS. 23 and 24, FIGS. 25 and 26, FIGS. 27 and 28, FIGS. 29 and 30 and in FIGS. 31 and 32, the section lines are A-A′, B-B′, C-C′, D-D′ ad E-E′, respectively.

[0170] Referring to FIGS. 22 to 24, the active matrix substrate according to the second embodiment is constructed in the following manner. The structure of the liquid crystal display apparatus except the active matrix substrate is the same as that of the first embodiment.

[0171] In an area of the planar surface of the insulating substrate 1, presenting the rough surface la in a preset area thereof, plural gate lines 2 are arranged parallel to one another. From each gate bus line 2 is branched a gate electrode 3. On the planar top surface in the rough surface 1 a on the insulating substrate 1, there is provided a projection member 26 formed of the same metal as the gate electrode 3, for example, Cr, Ta, Mo, Ti or Cr/Al. The projection member 26 serves as a basis in forming the rough surface of the reflector 4 along with the rough surface 1 a of the insulating substrate 1. Between the projection member 26 on the insulating substrate 1 and the gate electrode 3, there is formed a shorting prohibiting wiring 25, adapted for preventing shorting across the reflector 4 and the gate electrode 3 and for separating the projection member 26 from the gate electrode 3.

[0172] On the insulating substrate 1, including the gate electrode 3, a shorting prohibiting wiring 25 and the projection member 26, a gate insulating film 5 of SiN_(x) or SiO_(x) is formed. The gate insulating film 5 includes contact holes 27, 28, at preset positions on the shorting prohibiting wiring 25 for exposing this shorting prohibiting wiring 25. The gate insulating film 5 also includes, in its area on a roughened surface formed by the rough surface la and the projection member 26 of the insulating substrate 1, a rough surface on this surface. The contact hole 27 is a hole for electrically connecting the source electrode 8 and the shorting prohibiting wiring 25. The contact hole 28 is a hole for electrically interconnecting the transparent electrode 14 and the shorting prohibiting wiring 25.

[0173] On the gate insulating film 5, overlying the gate electrode 3, there is formed an island 7 comprised of a semiconductor layer 7 a and a contact electrode 7, stacked in this order.

[0174] Towards one end and the other end on the island 7, there are formed a source electrode 8 (8 a and 8 b) and a drain electrode 9 (9 a, and 9 b), respectively. The source electrode 8 is electrically connected through the contact hole 27 to the shorting prohibiting wiring 25. The drain electrode 9 is branched from a drain bus line 10 (10 a and 10 b) intersecting the gate bus line 2 through the gate insulating film 5.

[0175] In an area of the gate insulating film 5 overlying the rough surface 1 a of the insulating substrate, there is formed the reflector 4 which is formed of the same metal as the source electrode 8 or the drain electrode 9 and which serves for separating these electrodes from each other. The surface of the reflector 4 also has a rough surface substantially similar to the roughened surface formed by the rough surface 1 a and the projection member 26. For example, the maximum height of the surface roughness is of the order of 2 to 3 μm, with the distance between neighboring crests of the projection member being of the order of tens of μm. In the case of a semi-transmission type liquid crystal display apparatus, an aperture 4 c for transmitting a backlight are provided in an area of the rough surface of the reflector 4. In the case of a reflection type liquid crystal display apparatus, no aperture is provided in an area of the rough surface of the reflector 4. Meanwhile, the crests and recesses in the non-uniform, uneven or rough surfaces in the drawing, shown pointed, actually are rounded smoothly.

[0176] The gate electrode 3, gate-insulating film 5, island 7, source electrode 8 and the drain electrode 9 make up a thin film transistor 11 (TFT). This TFT 11 operates as a switching device.

[0177] A passivation film 12 is formed on the entire surface of the substrate including the TFT 11 and the reflector 4. The passivation film 12 includes a contact hole 28 corresponding to the contact hole in the gate insulating film 5 and has a rough surface corresponding to the rough surface of the reflector 4.

[0178] The transparent electrode 14 is formed in the area of the passivation film 12 presenting the rough surface. The transparent electrode 14, electrically connected through the contact hole 28 to the shorting prohibiting wiring 25, operates as a pixel electrode in conjunction with the reflector 4.

[0179] The production process for the active matrix substrate 15 in the liquid crystal display apparatus according to the second embodiment is now explained.

[0180] Referring first to FIGS. 16, 23a, 25 a, 27 a, 29 a and 31 a, a gate electrode layer (Cr layer, not shown), which later becomes underlying metal layers 2 a, 3 a, 17 a, 18 a, 19 a, 20 d, 20 e, 21 a, 25 and 26, is formed on the entire surface of the insulating substrate 1 having a planar surface.

[0181] Referring to FIGS. 16, 23a, 25 a, 27 a, 29 a and 31 a, a first mask 24 is formed on the gate electrode layer by a photolithography technique. Then, unneeded portions of the gate electrode layer are removed by for example dry etching or wet etching. This forms the gate bus line 2, gate electrode 3, underlying metal layer 17 a of the gate terminal unit, underlying metal layer 18 a of the drain terminal unit, underlying metal layer 19 a of the common terminal unit, gate electrodes 20 d, 20 e for the common device unit, common bus line 21 for the drain, shorting prohibiting wiring 25 and the projection member 26. At this stage, the first mask 24 has not been removed.

[0182] Referring to FIGS. 16, 23b, 25 b, 27 b, 29 b and 31 b, exposed sidewall sections of the gate bus line 2, gate electrode 3, underlying metal layer 17 a of the gate terminal unit, underlying metal layer 18 a of the drain terminal unit, underlying metal layer 19 a of the common terminal unit, gate electrodes 20 d, 20 e for the common device unit, common bus line 21 for the drain, shorting prohibiting wiring 25 and the projection member 26 and near-by surface portions of the insulating substrate 1 are covered by the first mask 24, by reflow processing, which is carried out to such an extent that only the first mask 24 is melted.

[0183] Since the distance between the gate electrode 3 and the shorting prohibiting wiring 25 is several μm and that between the neighboring projection members 26 is tens of μm, it is possible to make the first mask 24 continuous between the gate electrode 3 and the shorting prohibiting wiring 25 while making the first mask 24 non-continuous between the neighboring projection members 26.

[0184] Referring to FIGS. 17, 23c, 25 c, 27 c, 29 c and 31 c, a rough surface 1 a is formed at a preset area of the insulating substrate 1 by for example wet etching employing HF (hydrofluoric acid), sandblasting or dry etching employing CF₄ or O₂. The resulting product then is rinsed and the first mask removed. A broken line in FIG. 17 indicates a step 1 b of the insulating substrate. In this area, defined by the broken line in FIG. 17, the surface of the insulating substrate 1 is the original flat area, with an area lying outside the surrounded area being lower in level.

[0185] Such etching of the insulating substrate 1 in the step following the formation of for example the gate electrode 3 is meritorious in that, since HF is not interposed between e.g., the gate electrode and glass if the insulating substrate is formed of glass, it is possible to prevent peeling of e.g., the gate electrode.

[0186] Referring to FIGS. 18, 23d, 25 d, 27 d, 29 d and 31 d, a gate insulating film 5 of e.g., SiN_(x), an a-Si layer 7 a, which is to become a semiconductor layer, and an n⁺ type a-Si layer 7 b, which is to become a contact electrode, are sequentially formed on the entire surface of the insulating substrate 1 including the gate bus line 2, gate electrode 3, underlying metal layer 17 a of the gate terminal unit, underlying metal layer 18 a of the drain terminal unit, underlying metal layer 19 a of the common terminal unit, gate electrodes 20 d, 20 e for the common device unit, common bus line 21 for the drain, shorting prohibiting wiring 25 and the projection member 26.

[0187] Referring to FIGS. 18, 23d, 25 d, 27 d, 29 d and 31 d, a second mask, not shown, is formed on the n⁺ type a-Si layer 7 b by the photolithography technique. Then, unneeded portions of the a-Si layer 7 a and the n⁺ type a-Si layer 7 b are removed, by e.g., dry etching. The second mask then is removed to form islands 7 and 20 f.

[0188] Referring to FIGS. 19, 24e, 26 e, 28 e, 30 e and 32 e, a third mask, not shown, is formed on the gate insulating film 5, including the islands 7, and 20 f, by the photolithography technique. Then, unneeded portions of the gate insulating film 5 of an area which later become a contact hole are removed, by e.g., dry etching, until the Cr layers 2, 18 a, 20 e, 21 and 25 are partially exposed. The third mask then is removed. This forms contact holes 18 e, 20 c, 21 c and 27.

[0189] It is noted that the contact hole 18 e serves for partially exposing the Cr layer 18 a of the drain device unit. The contact hole 20 c serves for partially exposing the Cr layers 2, 20 a, 20 e and 21 of the common device unit. The contact hole 21 c serves for partially exposing the common bus line 21, while the contact hole 27 serves for partially exposing the shorting prohibiting wiring 25.

[0190] Referring to FIGS. 20, 24f, 26 f, 28 f, 30 f and 32 f, underlying metal layers 4 a, 8 a, 9 a, 10 a and 22 a (referred to below as ‘Cr’), and overlying metal layers 4 b, 8 b, 9 b, 10 b and 22 b (referred to below as ‘Al/Nd’), are deposited in this order, to form a source/drain electrode layer.

[0191] Referring to FIGS. 20, 24f, 26 f, 28 f, 30 f and 32 f, a fourth mask, not shown, is formed on the source/drain electrode layer, by a photolithography technique. Then, unneeded portions of the source/drain electrode layers are removed, such as by dry etching or wet etching. This forms the reflector 4, source electrode 8, drain electrode 9, and drain bus line 10, source/drain electrodes 20 a, 20 b for the common device unit and the common bus line 22 for the gate.

[0192] It is noted that, for the reflection type apparatus or the semi-transmitting type apparatus, the reflector 4 is or is not provided with an aperture, respectively. On the other hand, the reflector 4 is connected to the source electrode 8, while the source electrode 8 is connected through the contact hole 27 to the shorting prohibiting wiring 25. The source/drain electrodes 20 a, and 20 b for the common device unit are connected through the contact hole 20 c to the gate bus line 2, common bus line 21 for the drain or to the gate electrode 20 e of the common device unit. The common bus line 22 for the gate is connected through the contact hole 21 c to the common bus line 21 for the drain.

[0193] Then, using the metal layer, for example, the source electrode 8 or the drain electrode 9, and the fourth mask, as etching masks, the n⁺ type a-Si layer 7 b is etched. The fourth mask then is removed. This forms an ohmic contact layer.

[0194] Referring to FIGS. 21, 24g, 26 g, 28 g, 30 g and 32 g, a passivation film 12 is formed, such as by plasma CVD method, on the entire surface of the gate insulating film 5, including the source electrode 8, drain electrode 9, drain bus line 10, source/drain electrodes 20 a, and 20 b for the common device unit and the common bus line 22 for the gate and on the reflector 4.

[0195] Referring to FIGS. 21, 24g, 26 g, 28 g, 30 g and 32 g, a fifth mask, not shown, is formed on the passivation film 12 by a photolithography technique. Then, unneeded portions of the passivation film 12 or the gate insulating film 5 in an area which later becomes the contact hole are removed, such as by dry etching, until the Cr layers 17 a, 18 a, 19 a and 25 are partially exposed. The fifth mask then is removed. This forms the contact holes 17 c, 18 c, 19 b and 28.

[0196] It is noted that the contact hole 17 c serves for partially exposing the Cr layer 17 a of the gate terminal unit. The contact hole 18 c serves for partially exposing the Cr layer 18 of the drain terminal unit in an area other than the contact hole 18 e. The contact hole 19 b serves for partially exposing the Cr layer 19 a of the common terminal unit, while the contact hole 28 serves for partially exposing the shorting prohibiting wiring 25 in an area other than the contact hole 27.

[0197] Referring to FIGS. 22, 24h, 26 h, 28 h, 30 h and 32 h, transparent electrode layers 14, 17 d, 18 d and 19 c of, for example, ITO, are deposited, such as by sputtering, on the entire surface of the substrate, including the passivation film 12.

[0198] Referring to FIGS. 22, 24h, 26 h, 28 h, 30 h and 32 h, a sixth mask, not shown, is finally formed, such as by a photolithography technique, on the transparent electrode layers 14, 17 d, 18 d and 19 c. An excess portion of the transparent electrode layers is then removed such as by wet etching. This forms the transparent electrode 14, which later becomes the pixel electrode, the terminal 17 d of the gate terminal unit, terminal 18 d of the drain terminal unit and the terminal 19 c of the common terminal portion.

[0199] It is noted that the transparent electrode 14 is electrically connected to the shorting prohibiting wiring 25 through contact hole 28. The terminal 17 d of the gate terminal unit, the terminal 18 d of the drain terminal unit and the terminal 19 c of the common terminal unit are connected to the Cr layers 17 a, 18 a and 19 a of the respective portions through the contact holes 17 c, 18 c and 19 c of the respective portions.

[0200] The above process renders it possible to manufacture an active matrix substrate having a structure shown in FIG. 22. With the manufacturing method for the active matrix substrate according to the second embodiment, a reflection or semi-transmission type active matrix substrate, with an optimum display function, having a reflector presenting a rough surface, may be produced, using only six masks, thus achieving a process simplified by at least one PR step as compared to the conventional manufacturing method.

[0201] A third embodiment is now explained by referring to the drawings. FIGS. 33 to 38 are plan views schematically illustrating the manufacturing method for the active matrix substrate in a liquid crystal display apparatus according to the third embodiment of the present invention. FIG. 39a to FIG. 45g are cross-sectional views schematically illustrating the manufacturing process for the active matrix substrate in a liquid crystal display apparatus according to the third embodiment of the present invention. In FIGS. 39 and 40, FIGS. 41 and 42, FIG. 43, FIG. 44 and in FIG. 45, the section lines are A-A′, B-B′, C-C′, D-D′ and E-E′, respectively.

[0202] Referring to FIGS. 39 to 40, the active matrix substrate of the third embodiment is constructed as follows. It is noted that the structure of the liquid crystal display apparatus except the active matrix substrate is the same as that of the first embodiment.

[0203] In an area of the planar surface of the insulating substrate 1, presenting the rough surface 1 a in a preset area thereof, plural gate lines 2 are arranged parallel to one another. From each gate bus line 2 is branched a gate electrode 3. On the planar top surface in the rough surface 1 a on the insulating substrate 1, there are provided plural projection members 26 formed of the same metal as that of the gate electrode 3, for example, Cr, Ta, Mo, Ti or Cr/Al. The projection member 26 serve as a basis in forming the rough surface of the reflector 4 along with the rough surface 1 a of the insulating substrate 1.

[0204] On the insulating substrate 1, including the gate electrode 3 and the projection member 26, a gate insulating film 5 of SiN_(x) or SiO_(x) is formed. The gate insulating film 5 also includes, in an area of the surface lying on the rough surface formed by the rough surface 1 a and the projection member 26 of the insulating substrate 1, a rough surface.

[0205] On the insulating substrate 1 overlying the gate electrode 3, there is formed an island 7 comprised of a semiconductor layer 7 a and a contact electrode 7 b, stacked in this order.

[0206] Towards one end and the other end on the island 7, there are formed a source electrode 8 (8 a and 8 b) and a drain electrode 9 (9 a, and 9 b), respectively. The reflector 4 (4 a and 4 b) is formed, without separation, in the same layer as the source electrode 8, in an area on the gate insulating film 5 overlying the roughened surface formed by the rough surface 1 a of the insulating substrate 1 and the projection member 26. The surface of the reflector 4 presents a rough surface substantially similar to the roughened surface formed by the rough surface 1 a of the insulating substrate 1 and the projection member 26, with the maximum height of the surface roughness being on the order of two to three μm, with the separation between the crests of the neighboring projection member 26 being tens of μm. In the case of the semi-transmission type liquid crystal display apparatus, there are formed aperture 4 c in a portion of the area of the rough surface in the reflector 4 for transmitting the light rays of the backlight. In the case of the reflection type liquid crystal display apparatus, no aperture is provided in the area of the rough surface of the reflector 4. Although the crests and dents of the rough surface as shown in the drawings are seen to be pointed, these are actually rounded smoothly. The drain electrode 9 is branched from the drain bus lines 10 (10 a and 10 b) intersecting the gate bus line 2 via gate insulating film 5.

[0207] The gate electrode 3, gate-insulating film 5, island 7, source electrode 8 and the drain electrode 9 constitute a thin-film transistor (TFT) 11. This TFT 11 operates as a switching device.

[0208] On the entire surface of the substrate including the TFT 11 and the reflector 4, there is formed a passivation film 12 including a contact hole 6 in a preset area of the rough surface of the reflector 4, for exposing the Cr layer 4 a of the reflector 4, and in an area of the surface of the reflector 4, there is provided a rough surface lying on this rough surface.

[0209] In an area on the passivation film 12 having the rough surface, there is provided a transparent electrode 14 which connects to the reflector 4 through the first contact hole 6. The transparent electrode 14 operates, together with the reflector 4, as pixel electrodes.

[0210] The production process for the active matrix substrate in the liquid crystal display apparatus according to the third embodiment is now explained.

[0211] Referring first to FIGS. 33, 39a, 41 a, 43 a, 44 a and 45 a, a gate electrode layer (Cr layer, not shown), which later becomes underlying metal layers 2 a, 3 a, 17 a, 18 a, 19 a, 20 d, 20 e and 21 a, is formed on the entire surface of the insulating substrate 1 having a planar surface.

[0212] Referring to FIGS. 33, 39a, 41 a, 43 a, 44 a and 45 a, a first mask 24 is formed on the gate electrode layer by a photolithography technique. Then, unneeded portions of the gate electrode layer are removed by for example dry etching or wet etching. This forms the gate bus line 2, gate electrode 3, underlying metal layer 17 a of the gate terminal unit, underlying metal layer 19 a for the common terminal unit, gate electrodes 20 d, 20 e for the common device unit and the common bus line 21 for the drain. At this stage, the first mask 24 has not been removed.

[0213] Referring to FIGS. 33, 39b, 41 b, 43 b, 44 b and 45 b, exposed sidewall sections of the gate bus line 2, gate electrode 3, underlying metal layer 17 a of the gate terminal unit, underlying metal layer 19 a of the common terminal unit, gate electrodes 20 d, and 20 e for the common device unit and the common bus line 21 for the drain, and near-by surface portions of the insulating substrate 1, are covered by the first mask 24, by reflow processing, which is carried out to such an extent that only the first mask 24 is melted.

[0214] Referring to FIGS. 34, 39c, 41 c, 43 c, 44 c and 45 c, the rough surface 1 a is formed at a preset area of the insulating substrate 1 by for example wet etching employing HF (hydrofluoric acid), sandblasting or dry etching employing CF₄ or O₂. The resulting product then is rinsed and the first mask removed. The broken line in FIG. 34 indicates a step 1 b of the insulating substrate. In this area, defined by the broken line in the drawing, the surface of the insulating substrate 1 is the original flat area, with an area lying outside the surrounded area being lower in level.

[0215] Referring to FIGS. 35, 39d, 41 d, 43 d, 44 d and 45 d, a gate insulating film 5 of e.g., SiN_(x), an a-Si layer 7 a, which is to become a semiconductor layer and an n⁺ type a-Si layer 7 b which is to become a contact electrode, are sequentially formed on the entire surface of the insulating substrate 1 including the gate bus line 2, gate electrode 3, underlying metal layer 17 a of the gate terminal unit, underlying metal layer 19 a of the common terminal unit, gate electrodes 20 d, and 20 e for the common device unit and the common bus line 21 for the drain.

[0216] Referring to FIGS. 35, 39d, 41 d, 43 d, 44 d and 45 d, a second mask, not shown, is formed on the n⁺ type a-Si layer 7 b by the photolithography technique. Then, unneeded portions of the a-Si layer 7 a and the n⁺ type a-Si layer 7 b are removed, by e.g., dry etching. The second mask then is removed to form islands 7 and 20 f.

[0217] Then, referring to FIGS. 36, 40e, 42 e, 43 e, 44 e and 45 e, underlying metal layers 4 a, 8 a, and 9 a, 10 a and 22 a (referred to below as ‘Cr’), and metal overlying layers 4 b, 8 b, 9 b, 10 b and 22 b of, for example, Al (referred to below as ‘Al/Nd’ are deposited in this order on the entire surface of the insulating substrate to form a source/drain electrode layer, not shown.

[0218] Referring now to FIGS. 36, 40e, 42 e, 43 e, 44 e and 45 e, a third mask, not shown, is formed by the photolithography technique on a source/drain electrode layer. Then, unneeded portions of the source/drain electrode layer are removed by for example dry etching or wet etching. This forms the reflector 4, source electrode 8, drain electrode 9, drain bus line 10, source/drain electrode layers 20 a, 20 b for the common device unit, and the common bus line 22 for the gate.

[0219] In the case of the reflection type liquid crystal display apparatus, no aperture is provided in the rough surface in the reflector 4. In the case of the semi-transmission type liquid crystal display apparatus, there is formed an aperture 4 c. The reflector 4 is formed on the same layer with the source electrode 8 and is continuous to the source electrode 8.

[0220] Then, using the metal layers, inclusive of the source electrode 8 and the drain electrode 9, and the third mask, as etching masks, the n⁺ type a-Si layer 7 b is etched. The third mask then is removed to form an ohmic contact layer.

[0221] Then, referring to FIGS. 37, 40f, 42 f, 43 f, 44 f and 45 f, a passivation film 12 is formed, by e.g., the plasma CVD method, on the entire surface of the gate insulating film 5, inclusive of the reflector 4, source electrode 8, drain electrode 9, drain bus line 10, source/drain electrodes 20 a, 20 b for the common device part, and the common bus line 22 for the gate.

[0222] Then, referring to FIGS. 37, 40f, 42 f, 43 f, 44 f and 45 f, a fourth mask, not shown, is formed on the passivation film 12 by the photolithography technique. Then, unneeded portions of the passivation film 12, gate insulating film 5 or the Al/Nd layers 2 b, 4 b, 17 b, 19 a, 21 a, lying in an area which later becomes the contact hole, are removed, such as by dry etching, until the Cr layers 2 a, 4 a, 10 a, 17 a, 18 a, 19 a, 20 a, 20 d, 20 e, 21 a and 22 a are partially exposed. The fourth mask then is removed. This forms contact holes 6, 17 c, 18 c, 19 b, 20 c, 21 c and 22 c.

[0223] The contact holes 6, 17 c, 18 c, 19 b, 20 c, 21 c and 22 c are those for partially exposing the Cr layer 4 a of the reflector, the Cr layer 17 a of the gate terminal unit, the Cr layer 18 a of the drain terminal unit, the Cr layer 19 a of the common terminal unit, the Cr layers 2 a, 20 a, 20 d, 20 e, 21 a and 22 a of the common device unit, the Cr layer 21 a of the common bus line for the drain and those for partially exposing the Cr layer 22 a of the common bus line Cr for the gate, respectively.

[0224] Then, referring to FIGS. 38, 40g, 42 g, 43 g, 44 g and 45 g, on the entire substrate surface including the passivation film 12, the transparent electrode layers 14, 17 d, 18 d, 19 c, 20 g and 23 of ITO or the like are deposited, such as by sputtering method.

[0225] Finally, referring to FIGS. 38, 40g, 42 g, 43 g, 44 g and 45 g, a fifth mask, not shown, is formed on the transparent electrode layers 14, 17 d, 18 d, 19 c, 20 g and 23, such as by the photolithography technique. Then, unneeded portions of the transparent electrode layers are removed; such as by wet etching. The fifth mask then is removed. This forms the transparent electrode 14, as pixel electrodes, terminal 17 d of the gate terminal unit, terminal 18 d of the drain terminal unit, terminal 19 c of the common terminal unit, wiring 20 g of the common device unit and the wiring 23 across the common bus lines 21 and 22.

[0226] The transparent electrode 14 electrically connects to the Cr layer 4 a of the reflector through the contact hole 6. The terminal 17 d of the gate terminal unit, the terminal 18 d of the drain terminal unit and the terminal 19 c of the common terminal unit connect to the Cr layers 17 a, 18 a and 19 a of the respective units, respectively, through the contact holes 17 c, 18 c and 19 b of the respective units, respectively. Through the contact holes 20 c of optional combinations, the wiring 20 f of the common device unit electrically connects the gate bus line 2 to the source/drain electrode 20 a of the common device unit, while electrically connecting the common bus line 22 to the gate electrode 20 e of the common device unit, electrically connecting the common bus 21 to the source/drain electrode 20 a of the common device unit and electrically connecting the drain bus line 10 to the gate electrode 20 e of the common device unit. The wiring 23 across the common bus lines 21 and 22 electrically interconnects the common bus lines 21 and 22 through contact holes 21 c and 22 c.

[0227] The above process renders it possible to prepare the active matrix substrate having the structure shown in FIG. 38. With the method for producing the active matrix substrate according to the third embodiment, described above, it is possible to produce a reflection or semi-transmitting type active matrix substrate, having a reflector presenting a rough surface, and which exhibits optimum display performance, using only five masks, thus simplifying the production method by at least two PRs as compared to the conventional production method.

[0228] A fourth embodiment is now explained by referring to the drawings. FIGS. 46 to 52 are plan views schematically illustrating the manufacturing method for the active matrix substrate in a liquid crystal display apparatus according to the fourth embodiment of the present invention. FIG. 53a to FIG. 62h are cross-sectional views schematically illustrating the manufacturing process for the active matrix substrate in a liquid crystal display apparatus according to the fourth embodiment of the present invention. In FIGS. 53 and 54, FIGS. 57 and 58, FIG. 59, FIG. 60 and in FIGS. 61 and 62, the section lines are A-A′, B-B′, C-C′, D-D′ and E-E′, respectively.

[0229] Referring to FIGS. 52 to 54, the active matrix substrate according to the fourth embodiment is constructed as follows. It is noted that the structure of the liquid crystal display apparatus except the active matrix substrate is the same as that of the first embodiment.

[0230] In an area of the planar surface of the insulating substrate 1, presenting the rough surface 1 a in a preset area thereof, plural gate lines 2 are arranged parallel to one another. From each gate bus line 2 is branched a gate electrode 3.

[0231] A gate insulating film 5 of, for example, SiN_(x), is formed on the insulating substrate 1 including the gate electrode 3. On the planar surface of the insulating substrate 1, presenting the rough surface 1 a, there are provided plural projection members 5 a formed of the same metal as that of the gate insulating film, for example, SiN_(x) . Projection members 5 a serve as a basis in forming the rough surface of the reflector 4 along with the rough surface 1 a of the insulating substrate 1. Although not shown, plural projection members of the same metal as that of the gate electrode 3, such as Cr, may be provided between the top planar surfaces of the rough surface 1 a of the insulating substrate 1 and the projection members 5 a as in the second and third embodiment (refer to projection members 26 of FIGS. 23 and 39).

[0232] On the insulating substrate 1 overlying the gate electrode 3, there is formed an island 7 comprised of a semiconductor layer 7 a and a contact electrode 7 b, laminated in this order.

[0233] Towards one end and the other end on the island 7, there are formed a source electrode 8 (8 a and 8 b) and a drain electrode 9 (9 a, and 9 b), respectively. The drain electrode 9 is branched from the drain bus line 10 (10 a) intersecting the gate bus line 2 via gate insulating film 5.

[0234] The gate electrode 3, gate-insulating film 5, island 7, source electrode 8 and the drain electrode 9 constitute a thin-film transistor (TFT) 11. This TFT 11 operates as a switching device.

[0235] On the substrate inclusive of the TFT 11, there is formed a passivation film 12. The passivation film 12 includes contact holes 6, 13, in preset areas of the source electrode 8, for exposing its Cr layer 8 a. The contact hole 6 serves for electrically interconnecting the source electrode 8 a and the reflector 4 b, while the contact hole 6 serves for electrically interconnecting the source electrode 8 a and the transparent electrode 14. On the top of the projection member 5 a, there is provided a projection member 12 a formed of the same material as that of the passivation film 12, for example SiN_(x).

[0236] The reflector 4 (4 b) is formed in an area from the roughened surface formed by the rough surface 1 a of the insulating substrate 1 and the projection members 5 a and 12 a, or projection members by the Cr layer, up to an area overlying the passivation film 12 in turn overlying the TFT 11. The reflector 4 b overlying the roughened surface formed by the rough surface 1 a of the insulating substrate 1 and the by the projection members 5 a, 12 a, occasionally the projection members by the Cr layer, and the reflector 4 b overlying the TFT 11, are formed by the same process and are electrically conducting to each other. The surface of the reflector 4 presents a rough surface lying on the roughened surface formed by the rough surface 1 a of the insulating substrate 1 and by the projection members 5 a, 12 a, with the rough surface being of substantially the same shape as the roughened surface. The maximum height of the surface roughness is on the order of 2 to 3 μm, with the spacing between adjoining crests being on the order of tens of μm. In the case of the semi-transmission type liquid crystal display apparatus, there is formed an aperture 4 c in a portion of an area of the rough surface of the reflector 4 for transmitting the light rays from the backlight. In the case of the reflection type liquid crystal display apparatus, no aperture is provided in the rough surface in the reflector 4. Although the crests and dents of the rough surface and the rough surface as shown in the drawings are seen to be pointed these crests and groves are actually rounded smoothly.

[0237] On the reflector 4 and on an area of the passivation film 12 including the rough surface there is provided a transparent electrode 14, which transparent electrode 14 is electrically connected to the source electrode 8 through the contact hole 6. The transparent electrode 14 operates as pixel electrodes in conjunction with the reflector 4. When the transparent electrode 14 is formed in contact with the reflector 4, and the reflector 4 is formed of metal including Al, ITO as the material of the transparent electrode 14 is effective to prevent hillocks from being produced by Al. The transparent electrode 14 (ITO) is not optimum in electrical conductivity to the reflector 4 (Al/Nd) and hence is supplied with the power predominantly from the source electrode 8 (Cr).

[0238] The production process for producing the active matrix substrate in the liquid crystal display apparatus according to the fourth embodiment is hereinafter explained.

[0239] Referring first to FIGS. 46, 53a, 55 a, 55 a, 59 a and 61 a, a gate electrode layer (Cr layer, not shown), which is to become the underlying metal layers 2 a, 3 a, 17 a, 19 a, 20 d, 20 e and 21 a, is formed on the entire surface of the insulating substrate 1 having a planar surface.

[0240] Then, referring to FIGS. 46, 53a, 57 a, 55 a, 59 a and 61 a, a first mask, not shown, is formed on the gate electrode layer by the photolithography technique. Then, unneeded portions of the gate electrode layer are removed by for example dry etching or wet etching. The first mask then is removed. This sequentially forms the gate bus line 2, gate electrode 3, underlying metal layer 17 a for the gate terminal unit, underlying metal layer 19 a for the common terminal unit, gate electrodes 20 d, 20 e for the common device unit, and the common bus line 21 for the drain.

[0241] Then, referring to FIGS. 47, 53b, 55 b, 57 b, 59 b and 61 b, the gate insulating film 5 of, for example, SiN_(x), the a-Si layer 7 a, which becomes the semiconductor layer, and the n⁺ type a-Si layer 7 b, which becomes he contact electrode, are sequentially formed on the entire substrate surface comprising the gate bus line 2, gate electrode 3, underlying metal layer 17 a for the gate terminal unit, underlying metal layer 19 a for the common terminal unit, gate electrodes 20 d, and 20 e for the common device unit, and the common bus line 21 for the drain.

[0242] Then, referring to FIGS. 47, 53b, 55 b, 57 b, 59 b and 61 b, a second mask, not shown, is formed by the photolithography technique on the n⁺ type a-Si layer 7 b. Then, unneeded portions of the a-Si layer 7 a and the n⁺ type a-Si layer 7 b are removed, such as by dry etching, and subsequently the second mask is removed. This forms islands 7 and 20 f.

[0243] Then, referring to FIGS. 48, 53c, 55 c, 57 c, 59 c and 61 c, a source/drain electrode layer, not shown, comprised of metal layers 4 a, 8 a, 9 a, 10 a and 22 a of, for example, Cr (referred to below as ‘Cr’), is formed on the entire substrate surface.

[0244] Referring to FIGS. 48, 53c, 55 c, 57 c, 59 c and 61 c, a third mask, not shown, is formed on the source/drain electrode layer by the photolithography technique. Then, unneeded portions of the source/drain electrode layer are removed by for example dry etching or wet etching. This forms the source electrode 8, drain electrode 9, and drain bus line 10, source/drain electrodes 20 a and 20 b for the common device unit and the common bus line 22 for the gate.

[0245] Then, using the metal layers, such as source electrode 8 or drain electrode 9, and the third mask, as the etching masks, the n⁺ type a-Si layer 7 b is etched and subsequently the third mask is removed to form an ohmic contact layer.

[0246] Referring to FIGS. 49, 53d, 55 d, 57 d, 59 d and 61 d, the passivation film 12 is formed, by the plasma CVD method, on the entire surface of the gate insulating film 5, including the source electrode 8, drain electrode 9, drain bus line 10, source/drain electrodes 20 a and 20 b for the common device unit and the common bus line 22 for the gate.

[0247] Referring to FIGS. 49, 53d, 55 d, 57 d, 59 d and 61 d, a fourth mask 29 is formed on the passivation film 12, by the photolithography technique. Then, excess portions of the passivation film 12 or the gate insulating film 5, lying in an area which later becomes the contact hole, are removed by e.g., dry etching, until the insulating substrate 1 or Cr layers 2 a, 8 a, 10 a, 17 a, 18 a, 19 a, 20 a, 20 d, 20 e, 21 a and 22 a are partially exposed. This forms contact holes 6, 13, 17 c, 18 c, 19 b, 20 c, 21 c and 22 c and projection members 5 aand 12 a. At this stage, the fourth mask 29 has not been removed.

[0248] It is noted that the contact hole 6 partially exposes part of the source electrode 8 a. The contact hole 13 exposes part of the source electrode 8 a. The contact hole 17 c partially exposes part of the Cr layer 17 a of the gate terminal unit. The contact hole 18 c partially exposes part of the Cr layer 18 a of the drain terminal unit. The contact hole 19 b partially exposes part of the Cr layer 19 a of the common terminal unit. The contact hole 20 c partially exposes part of the Cr layers 2 a, 20 a, 20 d, 20 e, 21 a and 22 a of the common device unit. The contact hole 21 c partially exposes part of the Cr layer 21 a for the common bus line for the drain. The contact hole 22 c partially exposes part of the Cr layer 22 a of the common bus line for the gate.

[0249] Referring to FIGS. 49, 54e, 56 e, 58 e, 60 e and 62 e, exposed sidewall sections of the gate insulating film 5, passivation film 12 and the projection members 5 a, 12 a and near-by surface portions of the insulating substrate 1 are covered by the fourth mask 29, by reflow processing, which is carried out to such an extent that only the fourth mask 29 is melted. The contact holes 6, 13, 17 c, 18 c, 19 b, 20 c, 21 c and 22 c as well as the exposed surface portions of the Cr layers 2 a, 8 a, 10 a, 17 a, 18 a, 19 a, 20 a, 20 d, 20 e, 21 a, and 22 a are closed by the fourth mask 29.

[0250] Since the diameter of the contact hole including the surface of the Cr layer is on the order of several μm and the interval between the neighboring projection members 5 a and 12 a is tens of μm, it is possible to cover the surface of each contact hole including the surface of the Cr layer with the fourth mask 29 in such a manner that the fourth mask 29 is non-continuous between the neighboring projection members 5 aand 12 a. In this manner, the exposed surface not covered by the fourth mask 29 may be only the portion of the insulating substrate 1 between the respective projection members 5 a and 12 a.

[0251] Referring to FIGS. 50, 54f, 56 f, 58 f, 60 f and 62 f, a rough surface 1 a then is formed in a preset area of the insulating substrate 1 by wet etching, employing HF (hydrofluoric acid), sandblasting, or dry etching, employing CF₄ or O₂, a rough surface 1 a is formed. The resulting product is washed and the first mask is removed.

[0252] Referring to FIGS. 51, 54g, 56 g, 58 g, 60 g and 62 g, a layer of a reflector, formed by a metal layer 4 b of, for example, Al/Nd (referred to below as ‘Al/Nd’), is formed on the entire surface of the substrate including the passivation film 12.

[0253] Referring to FIGS. 51, 54g, 56 g, 58 g, 60 g and 62 g, a fifth mask, not shown, is formed, by the photolithography technique, on the layer of the reflector. Then, unneeded portions of the layer of the reflector are removed by for example dry etching or wet etching. The fifth mask then is removed. This forms the reflector 4 b.

[0254] In the case of the reflection type apparatus, no aperture is provided in the reflector 4, whereas, in the semi-transmission type apparatus, an aperture 4 c is provided in the reflector 4. The reflector 4 connects to the source electrode 8 through the contact hole 6. Since the reflector (Al/Nd) 4 is of a material different than the source electrode (Cr) 8, the layer of the reflector can be selectively etched, based on the difference in the selection ratio, so that the Cr layers 2 a, 8 a, 10 a, 17 a, 18 a, 19 a, 20 a, 20 d, 20 e, 21 a and 22 a can be exposed from the contact holes 13, 17 c, 18 c, 19 b, 20 c, 21 c, 22 c. On the other hand, the reflector 4 b, above the roughened surface formed by the rough surface 1 a and the projection members 5 a and 12 a, is electrically connected to the reflector 4 b above the TFT 11.

[0255] Referring to FIGS. 52, 54h, 56 h, 58 h, 60 h and 62 h, the transparent electrode layers 14, 17 d, 18 d, 19 c, 20 g and 23 of, for example, ITO, are deposited by for example sputtering on the entire substrate surface which includes the passivation film 12.

[0256] Finally, referring to FIGS. 52, 54h, 56 h, 58 h, 60 h and 62 h, a sixth mask, not shown, is formed, by the photolithography technique, on the transparent electrode layers 14, 17 d, 18 d, 19 c, 20 g and 23. Then, redundant portions of the transparent electrode layers are removed by for example wet etching. The sixth mask then is removed. This forms a transparent electrode 14 which later becomes pixel electrodes, a terminal 17 d of the gate terminal unit, a terminal 18 d of the drain terminal unit, a terminal 19 c of the common terminal unit, a wiring 20 g of the common terminal unit and a wiring 23 across the common bus lines 21 and 22.

[0257] It is noted that the transparent electrode 14 electrically connects to the source electrode 8 a through the contact hole 13. The terminal 17 d of the gate terminal unit, the terminal 18 d of the drain terminal unit and the terminal 19 c of the common terminal unit connect to the Cr layers 17 a, 18 a and 19 a of the respective units through contact holes 17 c, 18 c and 19 b of the respective units. Through two contact holes 20 c of an optional combination, the wiring 20 f of the common device unit electrically connects the gate bus line 2 to the source/drain electrode 20 a of the common device unit, while connecting the common bus line 22 to the gate electrode 20 e of the common device unit, connecting the common bus line 21 to the source/drain electrode 20 a of the common device unit and connecting the drain bus line 10 to the gate electrode 20 e of the common device unit. The wiring 23 across the common bus lines 21 and 22 electrically connects the common bus lines 21 and 22 across the contact holes 21 c and 22 c.

[0258] The above process renders it possible to manufacture an active matrix substrate having a structure shown in FIG. 52. With the manufacturing method for the active matrix substrate according to the fourth embodiment, a reflection or semi-transmission type active matrix substrate, with an optimum display function, having a reflector presenting a rough surface, may be produced, using only six masks, thus achieving a process simplified by at least one PR step as compared to the conventional manufacturing method.

[0259] A fifth embodiment of the present invention is now explained by referring to the drawings. FIGS. 63 to 68 are plan views schematically illustrating the manufacturing method for the active matrix substrate in a liquid crystal display apparatus according to the sixth embodiment of the present invention. FIG. 69a to FIG. 78h are cross-sectional views schematically illustrating the manufacturing process for the active matrix substrate in a liquid crystal display apparatus according to the fifth embodiment of the present invention. In FIGS. 69 and 70, FIGS. 71 and 72, FIG. 73, FIG. 74 and in FIGS. 75 and 76, the section lines are A-A′, B-B′, C-C′, D-D′ and E-E′, respectively.

[0260] Referring to FIGS. 68 to 70, the active matrix substrate according to the fifth embodiment is constructed as follows. It is noted that the structure of the liquid crystal display apparatus except the active matrix substrate is the same as that of the first embodiment.

[0261] In an area of the planar surface of the insulating substrate 1, presenting the rough surface 1 a in a preset area thereof, plural gate lines 2 are arranged parallel to one another. From each gate bus line 2 is branched a gate electrode 3.

[0262] On the insulating substrate 1, including a gate electrode 3, there is formed a gate insulating film 5 formed of, for example, SiN_(x) . On the planar top surface in the rough surface 1 a on the insulating substrate 1, there are provided projection members Sa formed of the same metal as the gate insulating film 5, such as SiN_(x). The projection members 5 a serve as the basis in forming the rough surface of a reflector 4 along with the rough surface 1 a of the insulating substrate 1. Between the projection members 5 a on the insulating substrate 1 and the gate electrode 3, there is formed a shorting prohibiting wiring 25 for preventing shorting across the reflector 4 and the gate electrode 3 and for separating the projection members 5 a from the gate electrode 3.

[0263] On the insulating substrate 1, including the gate electrode 3 and the shorting prohibiting wiring 25, a gate insulating film 5 of for example SiN_(x) is formed. The gate insulating film 5 includes contact holes 27 and 28, at preset positions on the shorting prohibiting wiring 25 for exposing this shorting prohibiting wiring 25. The contact hole 27 is a hole for electrically connecting the source electrode 8 and the shorting prohibiting wiring 25. The contact hole 28 is a hole for electrically interconnecting the transparent electrode 14 and the shorting prohibiting wiring 25.

[0264] On the gate insulating film 5 overlying the gate electrode 3, there is formed an island 7 comprised of a semiconductor layer 7 a and a contact electrode 7 b, laminated in this order.

[0265] Towards one end and the other end on the island 7, there are formed a source electrode 8 (8 a and 8 b) and a drain electrode 9 (9 a, 9 b), respectively. The source electrode 8 is electrically connected through the contact hole 27 to the shorting prohibiting wiring 25. The reflector 4 (4 a and 4 b) is formed, without separation in the same layer as the source electrode 8, in an area overlying the roughened surface formed by the rough surface 1 a of the insulating substrate 1 and the projection members 5 a. The surface of the reflector 4 presents a rough surface substantially similar to the roughened surface formed by the rough surface 1 a of the insulating substrate 1 and the projection member 26, with the maximum height of the surface roughness being on the order of two to three μm, with the separation between the crests of the neighboring projection member 26 being tens of μm. In the case of the semi-transmission type liquid crystal display apparatus, there is formed an aperture 4 c in a portion of the area of the rough surface in the reflector 4 for transmitting the backlight. In the case of the reflection type liquid crystal display apparatus, no aperture 4 c is provided in the area of the rough surface of the reflector 4. Although the crests and dents of the rough surface as shown in the drawings are seen to be pointed these crests and dents are actually rounded smoothly. The drain electrode 9 is branched from the drain bus line 10 (10 a, 10 b) intersecting the gate bus line 2 through the gate insulating film 5.

[0266] The gate electrode 3, gate-insulating film 5, island 7, source electrode 8 and the drain electrode 9 constitute a thin-film transistor (TFT) 11. This TFT 11 operates as a switching device.

[0267] On the entire surface of the substrate including the TFT 11 and the reflector 4, there is formed a passivation film 12. The passivation film 12 includes a first contact hole 28 corresponding to the contact hole 28 in the gate insulating film 5 for exposing the shorting prohibiting wiring 25. The contact hole 28 electrically connects the shorting prohibiting wiring 25 to the transparent electrode 14.

[0268] The transparent electrode 14, provided in an area including the passivation film 12, is electrically connected to the shorting prohibiting wiring 25 through the contact hole 28. The transparent electrode 14 operates as a pixel electrode along with the reflector 4.

[0269] The production process for producing the active matrix substrate in the liquid crystal display apparatus according to the fifth embodiment is hereinafter explained.

[0270] Referring first to FIGS. 63, 69a, 71 a, 73 a, 75 a and 77 a, a gate electrode layer (Cr layer, not shown), which is to become the underlying metal layers 2 a, 3 a, 17 a, 18 a, 19 a, 20 d, 20 e, 21 a and 25, is formed on the entire surface of the insulating substrate 1 having a planar surface.

[0271] Then, referring to FIGS. 63, 69a, 71 a, 73 a, 75 a and 77 a, a first mask, not shown, is formed on the gate electrode layer by the photolithography technique. Then, unneeded portions of the gate electrode layer are removed by for example dry etching or wet etching. The first mask then is removed. This sequentially forms the gate bus line 2, gate electrode 3, underlying metal layer 17 a for the gate terminal unit, underlying metal layer 19 a for the common terminal unit, gate electrodes 20 d, 20 e for the common device unit, common bus line 21 for the drain, and the shorting prohibiting wiring 25.

[0272] Then, referring to FIGS. 64, 69b, 71 b, 73 b, 75 b and 77 b, the gate insulating film 5 of, for example, SiN_(x), the a-Si layer 7 a, which becomes the semiconductor layer, and the n⁺ type a-Si layer 7 b, which becomes the contact electrode, are sequentially formed on the entire substrate surface comprising the gate bus line 2, gate electrode 3, underlying metal layer 17 a for the gate terminal unit, underlying metal layer 18 a for the drain terminal unit, underlying metal layer 19 a for the common terminal unit, gate electrodes 20 d, 20 e for the common device unit, common bus line 21 for the drain and the shorting prohibiting wiring 25.

[0273] Then, referring to FIGS. 64, 69b, 71 b, 73 b, 75 b and 77 b, a second mask, not shown, is formed by the photolithography technique on the n⁺ type a-Si layer 7 b. Then, unneeded portions of the a-Si layer 7 a and the n⁺ type a-Si layer 7 b are removed, such as by dry etching, and subsequently the second mask is removed. This forms islands 7, 20 f.

[0274] Referring to FIGS. 65, 69c, 71 c, 73 c, 75 c and 77 c, a third mask 30 is formed on the gate insulation film 5, including the islands 7 and 20 f, by the photolithography technique. Then, excess portions of the gate insulating film 5, lying in an area which later becomes the contact hole, other than the projection members 5 a, are removed by e.g., dry etching, until the Cr layers 2, 18 a, 20 e, 21 and 25 are partially exposed. This forms contact holes 18 e, 20 c, 21 c and 27. At this stage, the third mask 30 has not been removed.

[0275] It is noted that the contact hole 18 e partially exposes part of the Cr layer 18 a of the drain terminal unit. The contact hole 20 c partially exposes part of the Cr layers 2, 20 a, 20 e and 21 of the common device unit. The contact hole 21 c partially exposes part of the common bus line 21. The contact hole 27 partially exposes part of the shorting prohibiting wiring 25.

[0276] Referring to FIGS. 65, 69d, 71 d, 73 d, 75 d and 77 d, exposed sidewall sections of the gate insulating film 5 and the projection members 5 a and near-by surface portions of the insulating substrate 1 are covered by the third mask 30, by reflow processing, which is carried out to such an extent that only the third mask 29 is melted. The third mask 30 closes the contact holes 18 e, 20 c, 21 c and 27 as well as the exposed surface portions of the Cr layers 2, 18 e, 20 e, 21 and 25.

[0277] Since the diameter of the contact hole including the surface of the Cr layer is on the order of several μm, the spacing between the gate electrode 3 and the shorting prohibiting wiring 25 is several μm and the interval between the projection members 5 is tens of μm, it is possible for the third mask 30 to be non-continuous between the neighboring projection members 5 a and for the first masks 24 to be continuous between the gate electrode 3 and the shorting prohibiting wiring 25. In this manner, it becomes possible for only the portion of the insulating substrate 1 lying between the neighboring projection members 5 a to be the exposed surface not covered by the third mask 30. The reason why the contact hole is stopped up with the third mask 30 is that, if the metal layer is exposed from the contact hole, HF used for etching the insulating substrate (glass) might be permeated to the metal layer to etch the glass underlying the metal layer.

[0278] Referring to FIGS. 65, 70e, 72 e, 74 e, 76 e and 78 e, a rough surface la is formed in a preset area of the insulating substrate 1 by wet etching, employing HF (hydrofluoric acid), sandblasting, or dry etching, employing CF₄ or O₂. The resulting product is washed and the third mask is removed.

[0279] Referring to FIGS. 66, 70f, 72 f, 74 f, 76 f and 78 f, underlying metal layers 4 a, 8 a, 9 a, 10 a and 22 a (referred to below as ‘Cr’) are formed on the entire substrate surface including the gate insulating film 5, projection members 5 a and the island 7, and overlying metal layers 4 b, 8 b, 9 b, 10 b and 22 b of, for example, Al/Nd (referred to below as ‘Al/Nd’), are sequentially stacked in this order to form a source/drain electrode layer, not shown.

[0280] Referring to FIGS. 66, 70f, 72 f, 74 f, 76 f and 78 f, a fourth mask, not shown, is formed, by the photolithography technique, on the source/drain electrode layer. Then, unneeded portions of the source/drain electrode layer and the n⁺ type a-Si layer 7 b are removed by for example dry etching or wet etching. This forms the reflector 4, source electrode 8, drain electrode 9, and drain bus line 10, source/drain electrodes 20 a, 20 b for the common device unit and the common bus line 22 for the gate. At this stage, the fourth mask has not been removed.

[0281] In the case of the reflection type apparatus, no aperture is provided in the reflector 4, whereas, in the semi-transmission type apparatus, there is formed an aperture 4 c in the reflector 4. The reflector 4 is connected to the source electrode 8, which source electrode 8 is connected to the shorting prohibiting wiring 25 through the contact hole 27. The source/drain electrodes 20 a and 20 b for the common device unit are connected through the contact hole 20 c to the gate bus line 2, gate electrode 20 e of the common device unit or to the common bus line 22 for the gate. The common bus line 22 for the gate is connected through the contact hole 21 c to the common bus line 21 for the drain.

[0282] The n⁺ type a-Si layer 7 b then is etched, using the source electrode 8 a, drain electrode 9 a and the fourth mask, as etching masks. The fourth etching mask then is removed. This forms an ohmic contact layer.

[0283] Referring to FIGS. 67, 70g, 72 g, 74 g, 76 g and 78 g, a passivation film 12 is formed, by the plasma CVD method, on the entire surface of the gate insulating film 5, including the reflector 4, source electrode 8, drain electrode 9, drain bus line 10, source/drain electrodes 20 a and 20 b for the common device unit and the common bus line 22 for the gate.

[0284] Referring to FIGS. 67, 70g, 72 g, 74 g, 76 g and 78 g, a fifth mask, not shown, is formed on the passivation film 12, by the photolithography technique. Then, excess portions of the passivation film 12 or the gate insulating film 5, lying in an area which later becomes the contact hole, are removed by e.g., dry etching, until the Cr layers 17 a, 18 a, 19 a and 25 are partially exposed. The fifth mask then is removed. This forms contact holes 17 c, 18 c, 19 b and 28.

[0285] It is noted that the contact hole 17 c partially exposes part of the Cr layer 17 a of the gate terminal unit. The contact hole 18 c partially exposes part of the Cr layer 18 a of the drain terminal unit. The contact hole 19 b partially exposes part of the Cr layer 19 a of the common terminal unit, while the contact hole 28 exposes part of the shorting prohibiting wiring 25.

[0286] Referring to FIGS. 68, 70h, 72 h, 74 h, 76 h and 78 h, the transparent electrode layers 14, 17 d, 18 d, 19 c, 20 g and 23 of, for example, ITO, are deposited by for example sputtering on the entire substrate surface which includes the passivation film 12.

[0287] Finally, referring to FIGS. 68, 70h, 72 h, 74 h, 76 h and 78 h, a sixth mask is formed, by the photolithography technique, on the transparent electrode layers 14, 17 d, 18 d and 19 c. Then, unneeded portions of the transparent electrode layers are removed by for example wet etching. The sixth mask then is removed. This forms a transparent electrode 14 which later becomes pixel electrodes, a terminal 17 d of the gate terminal unit, a terminal 18 d of the drain terminal unit, and a terminal 19 c of the common terminal unit.

[0288] It is noted that the transparent electrode 14 electrically connects to the shorting prohibiting wiring 25 through the contact hole 28. The terminal 17 d of the gate terminal unit, the terminal 18 d of the drain terminal unit and the terminal 19 c of the common terminal unit connect to the Cr layers 17 a, 18 a and 19 a of the respective units through contact holes 17 c, 18 c and 19 b of the respective units.

[0289] The above process renders it possible to produce an active matrix substrate having a structure shown in FIG. 68. With the manufacturing method for the active matrix substrate according to the fifth embodiment, a reflection or semi-transmission type active matrix substrate, with an optimum display function, having a reflector presenting a rough surface, may be produced, using only six masks, thus achieving a process simplified by at least one PR(photolithography ) process as compared to the conventional manufacturing method.

[0290] The production process for the active matrix substrate in the liquid crystal display apparatus according to the sixth embodiment is now explained by referring to the drawings. FIGS. 79 and 80 are cross-sectional views schematically illustrating the manufacturing process for the active matrix substrate in the liquid crystal display apparatus of the sixth embodiment of the present invention.

[0291] Referring to FIG. 79a, a gate electrode layer, not shown, which later becomes layers 2 a, 3 a and 26 of metal, such as Cr, is formed on the entire surface of the insulating substrate 1 having a planar surface.

[0292] Referring to FIG. 79a, a first mask 24 is formed on the gate electrode layer by the photolithography technique. Then, unneeded portions of the gate electrode layer are removed by for example dry etching or wet etching. This forms the gate bus line 2 a, gate electrode 3 a and the projection member 26. At this stage, the first mask 24 has not been removed.

[0293] Referring to FIG. 79b, exposed portions of the sidewalls of the gate bus line 2 a, gate electrode 3 a and the projection member 26 and the near-by surface portions of the insulating substrate 1 are covered by the first mask 24 by reflow processing which is carried out to such an extent that only the first mask 24 is melted.

[0294] If now the spacing between neighboring projection members 26 is set to tens of μm, it is possible for the first masks 24 not to be continuous between neighboring projection members 26.

[0295] Then, referring to FIG. 79c, a rough surface 1 a is formed in a preset area of the insulating substrate 1 by e.g., dry etching, such as wet etching, employing HF (hydrofluoric acid), sandblasting, or dry etching, employing CF₄ or O₂. The resulting product is washed and the first mask is removed.

[0296] Then, referring to FIG. 79d, the gate insulating film 5 of for example SiN_(x), a-Si layer 7 a which later becomes the semiconductor layer, and the n⁺ type a-Si layer 7 b which later becomes the contact electrode, are sequentially formed on the entire surface of the substrate including the gate bus line 2 a and the gate electrode 3 a.

[0297] Then, referring to FIG. 79d, a second mask, not shown, is formed on the n⁺ type a-Si layer 7 b by the photolithography technique. Then, unneeded portions of the a-Si layer 7 a and the n⁺ type a-Si layer 7 b are removed such as by dry etching and subsequently the second mask is removed. This forms islands 7 a and 7 b.

[0298] Referring to FIG. 80e, a third mask, not shown, is formed on the gate insulating film 5 and on the n⁺ type a-Si layer 7 b, by the photolithography technique. Then, unneeded portions of the gate insulating film 5 are removed by for example dry etching, and subsequently the third mask is removed. This exposes the rough surface 1 a of the insulating substrate 1 and the projection member 26.

[0299] Then, referring to FIG. 80f, underlying metal layers 4 a, 8 a, 9 a and 10 a of for example Cr (referred to below as ‘Cr’), and overlying metal layers 4 b, 8 b, 9 b and 10 b of for example Al/Nd (referred to below as ‘Al/Nd’), are stacked in this order on the entire substrate surface to form a source/drain electrode layer. This source/drain electrode layer is provided on the rough surface 1 a of the insulating substrate 1.

[0300] Referring now to FIG. 80f, a fourth mask, not shown, is formed by the photolithography technique on a source/drain electrode layer. Then, unneeded portions of the source/drain electrode layer are removed by for example dry etching or wet etching. This forms the reflectors 4 a and 4 b, source electrodes 8 a and 8 b, drain electrodes 9 a and 9 b, and drain bus lines 10 a and 10 b. The reflectors 4 a and 4 b are formed on the same layer of the source electrodes 8 a and 8 b and are arranged in continuation to the source electrodes 8 a and 8 b.

[0301] Then, using the metal layers, such as source electrode 8 or the drain electrode 9, as etching masks, the n⁺ type a-Si layer 7 b is etched, and subsequently the fourth mask is removed to form an ohmic contact layer.

[0302] Then, referring to FIG. 80g, the passivation film 12 is deposited on the entire surface of the gate insulating film 5, including the reflector 4, a-Si layer 7 a, source electrode 8, drain electrode 9 and the drain bus line 10 by e.g., the plasma CVD method.

[0303] Referring to FIG. 80g, a fifth mask, not shown, is formed on the passivation film 12 by the photolithography technique liquid. Then, unneeded portions of the passivation film 12 and the gate insulating film 5, lying in an area which later becomes the contact hole, are removed by for example dry etching, until the Cr layer 3 a is partially exposed. The fifth mask then is removed to form the contact hole 6. This contact hole partially exposes the Cr layer 4 a of the reflector.

[0304] Then, referring to FIG. 80h, the transparent electrode layer 14 of for example ITO is deposited, such as by sputtering, on the entire surface of the substrate, including the passivation film 12.

[0305] Referring to FIG. 80h, a sixth mask, not shown, is finally formed, such as by a photolithography technique, on the transparent electrode layer 14, and excess portions of the transparent electrode layers are then removed, such as by wet etching. The sixth electrode then is removed. This forms the transparent electrode 14, which later becomes the pixel electrodes. The transparent electrode 14 is electrically connected through the contact hole 6 to the reflector 4.

[0306] The above process enables the active matrix substrate shown in FIG. 80h to be produced. Thus, with the method for the preparation of the active matrix substrate according to the seventh embodiment, a reflection or semi-transmission type active matrix substrate, with an optimum display function, having a reflector presenting a rough surface, may be produced, using only six masks, thus achieving a process simplified by at least one PR step as compared to the conventional manufacturing method.

[0307] The meritorious effects of the present invention are summarized as follows.

[0308] The present invention make it possible to produce an active matrix substrate having a reflector exhibiting optimum reflection performance, using only five or six masks, thus reducing the cost of the active matrix substrate.

[0309] This is made possible by reduction in the number of process steps, in turn made possible by effective utilization of the masks used in etching the gate electrode layer, gate insulating film, a-Si layer or the source/drain electrode layer by for example reflow processing to form plural recesses in the insulating substrate, and by forming excess portions of the metal layers, insulating layers or semiconductor layers as protrusions in the insulating substrate, in addition to the recesses. In this manner, a rough surface having pronounced inundations is produced by the recesses and protrusions to form a reflector exhibiting optimum reflection characteristics, in which the maximum height of the surface roughness is on the order of 1 to 3 μm. Moreover, with the PR used for forming the TFT can be formed not only the recesses and protrusions but also the common terminal unit and the common device unit.

[0310] It should be noted that other objects, features and aspects of the present invention will become apparent in the entire disclosure and that modifications may be done without departing the gist and scope of the present invention as disclosed herein and claimed as appended herewith.

[0311] Also it should be noted that any combination of the disclosed and/or claimed elements, matters and/or items might fall under the modifications aforementioned. 

What is claimed is:
 1. A method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing said first substrate, and a liquid crystal layer placed between said first substrate and said second substrate; said method comprising: a first step of forming an etching mask, patterned to a predetermined shape, on at least one of a metal layer, an insulating layer and a semiconductor layer, formed on said insulating substrate; a second step of etching at least one of said metal layer, insulating layer and the semiconductor layer, using said etching mask, to expose portions of said insulating substrate and to form on said insulating substrate at least a constituent portion of said thin film transistor and a plurality of protrusions separated from said constituent portion; a third step of causing only said etching mask to reflow to cover exposed part of said constituent portion of said thin film transistor and near-by surface portions of said insulating substrate with said etching mask and to cover exposed surfaces of said protrusions and near-by surface portions of said insulating substrate under exposing surface portions of said insulating substrate located between neighboring protrusions; a fourth step of etching said insulating substrate, following said third step, using said etching mask to form one or more recesses in exposed areas of said insulating substrate; and a fifth step of selectively forming a reflector having a rough surface on a rough surface formed at least by said protrusions and recesses.
 2. The method as defined in claim 1 in which a metal layer and an insulation layer are formed in this order on said insulating substrate, said method comprising: etching said insulating layer in said second step, using said etching mask, to expose portions of said metal layer; and said contact hole being stopped up with said etching mask by reflow of said etching mask in said third step.
 3. The method as defined in claim 1 further comprising: a sixth step following said fourth step and previous to said fifth step, said sixth step forming another insulating layer having a rough surface on a rough surface at least formed by said protrusions and recesses.
 4. A method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing said first substrate, and a liquid crystal layer placed between said first substrate and said second substrate; said method comprising: a first step of etching a metal layer, using a first etching mask, following the formation of said metal layer on said insulating substrate, to expose a portion of said insulating substrate and to form a gate electrode; a second step of forming an insulating layer on said insulating substrate including said gate electrode and subsequently etching said insulating layer, using a second etching mask, to expose portions of said insulating substrate and to form a gate insulating film and a plurality of protrusions separated from said gate insulating film; a third step of causing only said etching mask to reflow to cover exposed portions of said gate insulating film and near-by surface portions of said insulating substrate with said etching mask and to cover exposed surfaces of said protrusions and near-by surface portions of said insulating substrate, with exposing the surface portions of said insulating substrate between neighboring protrusions; a fourth step of etching said insulating substrate, following said third step, using said etching mask, to form one or more recesses in exposed areas of said insulating substrate; and a fifth step of selectively forming a reflector having a rough surface on a rough surface formed at least by said protrusions and recesses.
 5. The method as defined in claim 4 further comprising a sixth step of forming a semiconductor layer on said insulating layer following formation of said insulating layer and prior to using said second etching mask in said second step, and of subsequently etching said semiconductor layer, using a third etching mask, to form an island above said gate electrode.
 6. The method as defined in claim 4 wherein the reflector formed in said second step is directly arranged on said rough surface formed by said protrusions and recesses.
 7. The method as defined in claim 5 wherein said reflector is of a laminated structure comprised of a lower Cr layer and an upper Al/Nd layer: the source electrode and the drain electrode of said laminated structure are selectively formed when said reflector is formed in said fifth step; a contact hole for partially exposing said Cr layer of said source electrode is formed in an other insulation layer formed on said insulating layer comprised of said reflector, source electrode and the drain electrode, and in said Al/Nd layer, after forming said other insulating layer; and wherein a transparent electrode layer electrically connecting to said source electrode through said contact hole is selectively formed on said other insulating layer.
 8. A method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing said first substrate, and a liquid crystal layer placed between said first substrate and said second substrate; said method comprising: a first step of forming a first metal layer on said insulating substrate and subsequently etching said first metal layer, using a first etching mask, to expose a portion of said insulating substrate and to form a gate electrode; a second step of forming a first insulating layer and a semiconductor layer in this order on said insulating substrate including said gate electrode and of subsequently etching said semiconductor layer using a second etching mask to form an island above said gate electrode; a third step of forming a second metal layer on said first insulating layer including said island and of subsequently etching said second metal layer using a third etching mask to form said source electrode and the drain electrode; a fourth step of forming a second insulating layer on said first insulating layer including said source electrode and the drain electrode and of subsequently etching said second insulating layer and the first insulating layer, using a fourth etching mask, to expose a portion of said insulating substrate and to form a plurality of protrusions; a fifth step of causing only said fourth etching mask to reflow following said fourth step to cover exposed surface portions of said first and second insulating layers and near-by surface portions of said insulating substrate with said fourth etching mask and to cover exposed surface portions of said protrusions and near-by surface portions of said insulating substrate with said fourth etching mask while exposing surface portions of said insulating substrate located between neighboring protrusions; a sixth step of etching said insulating substrate, using said fourth etching mask, following said fifth step, to selectively form one or more recesses in an exposed area of said insulating substrate; and a seventh step of selectively forming a reflector, having a rough surface on a rough surface formed at least by said protrusions and recesses.
 9. A method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on a predominantly planar insulating substrate, a second substrate having a transparent electrode and mounted facing said first substrate, and a liquid crystal layer placed between said first substrate and said second substrate; said method comprising: a first step of etching said planar insulating substrate, using a first etching mask, to selectively form a rough surface in a preset area of said insulating substrate; and a second step of etching said metal layer, using a second etching mask, for selectively forming a gate electrode on a planar area of said insulating substrate, and for selectively forming a reflector having a rough surface overlying a rough surface of said insulating substrate on said rough surface and in isolation from said gate electrode.
 10. A method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing said first substrate, and a liquid crystal layer placed between said first substrate and said second substrate; said method comprising: a first step of forming a first metal layer on said insulating substrate and subsequently etching said first metal layer using a first etching mask, to expose a portion of said insulating substrate, and to form a gate electrode, a plurality of protrusions being separated therefrom, and a wiring isolated from said gate electrode and said protrusions; a second step of causing only said first etching mask to reflow to cover exposed surfaces of said gate electrode and said wiring and nearby surface portions of said insulating substrate with said first etching mask and to cover exposed surfaces of said protrusions and near-by surface portions of said insulating substrate with said first etching mask; a third step of etching said insulating substrate, using said first etching mask, after said second step, to form one or more recesses in the exposed area of said insulating substrate; a fourth step of etching said semiconductor layer, using a second etching mask, after forming a first insulating film and a semiconductor layer on said insulating substrate, including said gate electrode, said protrusions and said wiring, to form an island above said gate electrode; a fifth step of etching said first insulating layer, using a third etching mask, to expose a portion of said wiring to form a first contact hole; a sixth step of etching a second metal layer, using a fourth etching mask, after forming said second metal layer on said first insulating layer, including said island, to form a source electrode, a drain electrode and a reflector, to electrically connect said source electrode through said first contact hole with said wiring; a seventh step of forming, after forming a second insulating layer on said first insulating layer including said source electrode, drain electrode and the reflector, a second contact hole in said second insulating layer and in said first insulating layer, using a fifth etching mask, for exposing a portion of said wiring; and an eighth step of selectively forming a transparent electrode layer on said second insulating layer for electrically connecting to said wiring through said second contact hole.
 11. A method for producing a liquid crystal display apparatus having a first substrate including a thin film transistor and a reflector on an insulating substrate, a second substrate having a transparent electrode and mounted facing said first substrate, and a liquid crystal layer placed between said first substrate and said second substrate; said method comprising: a first step of forming a first metal layer on said insulating substrate and subsequently etching said first metal layer, using a first etching mask, to expose a portion of said insulating substrate, and to form a gate electrode and a wiring separated from said gate electrode; a second step of forming a first insulating layer and a semiconductor layer in this order on said insulating substrate including said gate electrode and said wiring, and subsequently etching said semiconductor layer, using a second etching mask, to form an island above said gate electrode; a third step of etching said first insulating layer, using a third etching mask, to form a first contact hole which exposes a portion of said wiring, of exposing a portion of said insulating substrate and of forming a plurality of protrusions; a fourth step of causing only said third etching mask to reflow to cover the exposed surface portions of said first insulating layer and near-by surface portions of said insulating substrate with said third etching mask, to stop up said first contact hole with said third etching mask and to cover the exposed surface portions of said protrusions and near-by surface portions of said insulating substrate with said third etching mask, while exposing a part of the surface of said insulating substrate between neighboring protrusions and near-by surface portions of said insulating substrate; a fifth step of etching said insulating substrate, after said fourth step, using said third etching mask, to form one or more recesses in an exposed area of said insulating substrate; a sixth step of forming a second metal layer on said first insulating layer including said island, on said protrusions and on said recesses, and subsequently etching said second metal layer, using a fourth etching mask, to form a source electrode, a drain electrode and a reflector, to connect said source electrode electrically to said wiring through said first contact hole; a seventh step of forming a second insulating layer on said first insulating layer including said source electrode, drain electrode and the reflector, and subsequently forming a second contact hole, which exposes a portion of said wiring to said second insulating layer and the first insulating layer, using a fifth etching mask; and an eighth step of selectively forming a transparent electrode layer on sad second insulating layer for electrically connecting to said wiring 45 through said second contact hole.
 12. The method as defined in claim 1 wherein said etching mask is a photo resist.
 13. The method as defined in claim 1 wherein there is arranged an aperture at a preset area on the rough surface of said reflector.
 14. The method as defined in claim 4 wherein there is arranged an aperture at a preset area on the rough surface of said reflector.
 15. The method as defined in claim 8 wherein there is arranged an aperture at a preset area on the rough surface of said reflector.
 16. The method as defined in claim 9 wherein there is arranged an aperture at a preset area on the rough surface of said reflector.
 17. The method as defined in claim 10 wherein there is arranged an aperture at a preset area on the rough surface of said reflector.
 18. The method as defined in claim 11 wherein there is arranged an aperture at a preset area on the rough surface of said reflector. 